向镀液中加入氟化物,采用硫酸镍代替碳酸镍作为镍源,开发出一种镁合金化学镀镍新工艺.测定了该镀层中的磷含量及其耐蚀性、显微硬度、结合力,并用扫描电镜对其表面形貌进行了观察.结果表明,该镀层结合力合格,硬度远高于镁合金基体,且与普通化学镀层相当;该镀层属高磷镀层,耐蚀性较好,但与普通基体材料上的化学镀层相比要差一些.该工艺使镁合金化学镀成本大大降低,工艺得到简化.
参考文献
| [1] | Delong H K .Electroless Nickel Plating[P].US 3,152,009,1964. |
| [2] | ASTM B480-88. Standard guide for preparation of magnesium and magnesium alloys for electroplating[M]. |
| [3] | Dennis J K;Wan M K Y Y;Wake S J .Plating on magnesium alloy die castings[J].Transactions of the Institute of Metal Finishing,1985,63:74-80. |
| [4] | Olsen A L;Halvorsen S T .Method for the electrolytical metal coating of magnesium articles[P].European Patent Application: 030305,1981. |
| [5] | Delong H K .Plating on magnesium[M].Metal Finishing guideline,1978,76(01):175-183. |
| [6] | 刘新宽;向阳辉;胡文彬 等.镁合金化学镀液的长周期使用[J].中国有色金属学报,2003,13(04):1046-1050. |
| [7] | 向阳辉,胡文彬,沈彬,赵昌正,丁文江.镁合金直接化学镀镍的初始沉积机制[J].上海交通大学学报,2000(12):1638-1640. |
| [8] | Kerr C.Corrosion Resistance Testing of Electroless Nickel Coatings on Mild Steel[A].Cincinnati,Ohio,1997:1-19. |
| [9] | Ruffini A;Aleksinas M.The Corrosion Resistance of Electroless Nickel: A Review[A].Cincinnati,Ohio,1989:1-17. |
| [10] | Deng H;Moller P .Effect of the Substrate Surface Morphology on the Porosity of Electroless Nickel Coatings[J].Transactions of The Institute of Metal Finishing,1993,71(04):142-147. |
| [11] | Reade G W;Kerr C;Barker B D et al.The Importance of Substrate Surface Condition in Controlling the Porosity of Electroless Nickel Deposits[J].Transactions of the Institute of Metal Finishing,1998,76(04):149-155. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%