利用等离子体辅助电孤沉积技术制备了不同成分的TiAlSiN多元薄膜,并研究了Si含量对薄膜组织结构、显微硬度和耐磨性的影响.XRD物相分析表明:薄膜主要由AlN和TiN组成.随着膜层中Si含量的增加,薄膜的结构由明显的柱状晶转变为致密的玻璃态结构,显微硬度逐渐提高,耐磨性能得到明显改善.
参考文献
| [1] | INOUNE H;CHIDA H;HIOKI A.Structure and composition of (Ti,Al)N flims prepared r.f.planar magnetron sputtering using a composite target[J].Thin Solid Films,1995(271):15-18. |
| [2] | NORDIN M;LARSSON M;HOGMARK S .Mechanical and Tribological Properties of Muti-layered PVD Ti/CrN[J].Wear,1999,232:211-225. |
| [3] | OTANI Y;HOFMANM S .High temperature oxidation behaviour of (Ti1-xCry)N coatings[J].Thin Solid Films,1996,287:188-192. |
| [4] | 曾鹏,胡社军,谢光荣,黄拿灿,吴起白.多弧离子镀（Ti,W）xN合金涂层组织与性能[J].材料工程,2000(09):33-35,41. |
| [5] | MA S;PROCHAZKA J;KARVANKOVA J P et al.Comparative study of the tribological behavior of superhard nanocomposite coatings nc-TiN/a-Si3N4 with TiN[J].Surface Technology,2005,194:143-148. |
| [6] | Veprek S.;Jilek M. .Super- and ultrahard nanacomposite coatings: generic concept for their preparation, properties and industrial applications[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2002(3/4):443-449. |
| [7] | HOLUBAR P;JILEK M;SINA M .Nanocomposite nc-TiAlSiN and nc-TiN-BN coatings:their applications on subatrates made of cemented carbide and results of cutting tests[J].Surface Technology,1999,120:184-188. |
| [8] | 李争显,骆瑞雪,周慧.离子镀厚金膜过渡层的研究[J].稀有金属材料与工程,2001(06):460-462. |
| [9] | S. Veprek .New development in superhard coatings: the superhard nanocrystalline-amorphous composites[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,1998(1/2):449-454. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%