研究了电流退火的电流密度、退火时间对钴基和铁基非晶软磁合金条带有效磁导率的影响,并与等温退火处理的结果作了比较.结果表明:电流退火可以明显提高钴基和铁基非晶软磁合金条带的有效磁导率,且存在一个最佳电流密度、退火时间值,以使有效磁导率提高最大;铁基非晶软磁合金有效磁导率的提高明显优于钴基非晶软磁合金;电流退火提高钴基和铁基非晶软磁合金有效磁导率的幅度与等温退火基本相当,具有升温和降温速度快、退火效率高的优势.
参考文献
| [1] | Le ment W K;Willens R;Duwez P .Non-crystalline structure in solidified gold-sillion alloys[J].Nature,1960,187:869-870. |
| [2] | Mohri K.;Kohsawa T. .Magneto-inductive effect (MI effect) in amorphous wires[J].IEEE Transactions on Magnetics,1992(5):3150-3152. |
| [3] | Shen L.P.;Uchiyama T. .Sensitive stress-impedance micro sensor using amorphous magnetostrictive wire[J].IEEE Transactions on Magnetics,1997(5):3355-3357. |
| [4] | L. P. Shen;K. Mohri;A. L. X. Abudukelimu;H. Aoyama .Mechano-encephalogram based on amorphous wire micro SI acceleration sensor[J].IEEE Transactions on Magnetics,2001(4 Pt.1):2007-2009. |
| [5] | Mohri K .Application of amorphous magnetic to computer peripherals[J].Materials and Engineering,1994,A185:141-145. |
| [6] | 陈晨 .铁基软磁合金薄带的巨磁阻抗效应[D].山东大学,1997. |
| [7] | 丁昂,张延松,钱坤明,纪松.纳米晶软磁材料磁性温度稳定性与退火温度的关系[J].兵器材料科学与工程,2005(02):54-57. |
| [8] | 黎阳,严彪,杨磊,陆伟.铁基纳米晶软磁合金起始磁导率的研究[J].材料导报,2004(03):81-84. |
| [9] | 纪松;杨国斌;王润 .退火时间对Fe73.5Cu1.0Mo3.0Si13.5B9纳米软磁合金的结构与磁性的影响[J].金属材料研究,1995,21(03):25-28. |
| [10] | 纪松 .铁基超微晶软磁合金的结构与性能研究[D].北京科技大学,1994. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%