经实验摸索再经均匀试验和正交试验研究.找出了热电材料ZnO的热压烧结工艺.试验结果表明:所用的热压烧结工艺可明显地降低压制压力、烧结温度及缩短烧结时间,具有显著的活化烧结功效;且可保持原有的组织结构.热压烧结体组织疏松、有较多的孔隙,是降低热导率提高热电性能的有效措施和良好结果.

参考文献

[1] 李瑜煜,张仁元.热电材料热压烧结技术研究[J].材料导报,2007(07):126-129.
[2] Groza J R .Sintening of nanocrystalline powders[J].Powder Metallurgy,1999,35(07):59-66.
[3] Bauer R E .Sinter-HIP furnaces sintering and compactingin a combined cycle[J].Modem Development in Powder Metallurgy,1988,18(06):5-10.
[4] Shixue song.Repetitious-hot-pressing technique in hot-pressing process[M].School of Mechanical Engineering,Shandong University,2002:15-18.
[5] 王盘鑫.粉末冶金学[M].北京:冶金工业出版社,2004:233-236.
[6] 黄培云.粉末冶金原理[M].北京:冶金工业出版社,1991:334-340.
[7] Mikio Ito;Tomoya Nagira;Daisuke Furumoto;Yoshimitsu Oda;Shigeta Hara .Synthesis of Na_xCo_2O_4 thermoelectric oxide with crystallographic anisotropy by chemical solution process[J].Science and technology of advanced materials,2004(1/2):125-131.
[8] 高敏;张景韶.温差电转换及其应用[M].北京:兵器工业出版社
[9] 李云雁;胡传荣.试验设计与数据处理[M].北京:化学工业出版社,2005:79-118.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%