用扫描电镜上的EBSD装置研究化学气相沉积法制备的高纯钨的晶体取向,化学气相沉积钨具有{110}<001取向织构;用电子万能试验机和分离式霍普金森杆(SHPB)研究纯钨的准静态(10-3s-1)和动态(2000～5000 s-1)压缩力学性能.并与等轴晶重熔钨进行对比分析,沉积钨的屈服强度由静态时的1350 MPa上升到动态时的2000 MPa以上.是应变率敏感材料,等轴晶纯钨的静动态屈服强度高于柱状晶沉积纯钨,柱状晶沉积纯钨有明显的应变硬化效应.沉积钨柱状晶组织的塑性变形方式除滑移外,还有大量的孪晶产生.
参考文献
| [1] | 韩欢庆,陈飞雄,甘乐,褚征军.钨在药型罩中的应用[J].中国钨业,2004(01):26-28. |
| [2] | 马捷,张好东,毕安园,王从曾,周美玲.化学气相沉积法制取异型钨制品研究[J].兵工学报,2006(02):315-319. |
| [3] | Dummer T;Lasalvia J C;Ravichandaran G .Effect of strain rate on plastic flow and failure in polyerystalline tungsten[J].Acta Metallurgy,1998,46:6267-6290. |
| [4] | Wei Q;Jiao T .Mechanical behavior and dynamic failure of high-strength uhrafine grained tungsten under uniaxial cempression[J].Acta Materialia,2006,54:77-87. |
| [5] | Pappu S;SCn S .Deformation twins in oriented,eolumnargrain-ed tungsten rod ballistic penetrators[J].Materials Science and Engineering,2001,A298:144-157. |
| [6] | Argon A S;Maloof S R .Plastic deformation of tungsten single crystals at low temperatures[J].Acta Metallurgica,1966,14:1449-1462. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%