用改进燃烧合成法制备的α、β不同相含量的氮化硅粉料,通过配比组成多组不同相含量的粉科.经过混料、成型、烧结、密度测试.考察烧结温度对各组粉料烧结密度的影响;并对比了A、B两种不同烧结助剂配方.结果表明,多数粉料在1740～1780℃的温区内烧结密度达到峰值,烧结密度在97%以上.A配方适合于β-Si3N4粉、B配方相对更适合于α-si3N4粉.采用A配方,处理后的B相粉料烧结几乎完全致密,且烧结致密温区下移并变宽.粉料的团聚影响素坯密度,晶粒粗大的粉料则不利于成型.
参考文献
| [1] | 王守仁,耿浩然,王英姿.Si3N4/Al-Mg复合材料的无压浸渗制备技术[J].兵器材料科学与工程,2006(02):9-12. |
| [2] | 陈宏,穆柏春,郑黎明.氮化硅微粉制备技术[J].辽宁工学院学报,2006(03):191-195. |
| [3] | Jiang Yong;Wu Laner;Wang Peiling et al.Pretreatment and sintering of Si3N4 powder synthesized by the high-temperature self-propagation method[J].Materials Research Bulletin,2008,44(01) |
| [4] | De Pablos A;Osendi M I;Miranzo P.Correlation between microstructure and toughness of hot pressed Si3N4 ceramics seeded with β-Si3N4 particles[J].Ceramics International,2003(29):757-764. |
| [5] | X.D. Zhang;C.L. Liu;M.L. Guo;W.X. Li;L.J. Yin;Y.Y. Lue;Z. Wang;P. Wu;T.Y. Liu;M.K. Li;B. Yuan .Structural and optical properties of Cu nanoparticles embedded in Si_3N_4/Si by ion implantation[J].Optical materials,2008(9):1382-1386. |
| [6] | Traverse, A;Humbert, C;Six, C;Gayral, A;Busson, B .Nonlinear optical properties of Ag nanoparticles embedded in Si3N4[J].EPL,2008(6):640041-64004:5. |
| [7] | Amaral M;Lopes MA;Santos JD;Silva RF .Wettability and surface charge of Si3N4-bioglass composites in contact with simulated physiological liquids.[J].Biomaterials,2002(20):4123-4129. |
| [8] | 丁迎春,徐明,潘洪哲,沈益斌,祝文军,贺红亮.γ-Si3N4在高压下的电子结构和物理性质研究[J].物理学报,2007(01):117-122. |
| [9] | 陈义祥,林志明,李江涛,杜吉胜,杨树亮.PTFE添加剂对燃烧合成氮化硅的影响[J].稀有金属材料与工程,2007(z3):661-664. |
| [10] | 杨筠,陈义祥,林志明,李江涛.低氮气压力下燃烧合成α-Si3N4粉体[J].硅酸盐学报,2008(01):1-5. |
| [11] | 陈松林,杨筠,林志明,李江涛,赵海雷,孙加林.控温活化燃烧合成α-Si3N4的动力学研究[J].无机材料学报,2004(06):1345-1352. |
| [12] | 王华彬,张学忠,韩杰才,杜善义,DU Shan-yi.自蔓延高温合成氮化硅的生长机理[J].材料科学与工艺,2001(01):64-67. |
| [13] | 张玉军;张伟儒.结构陶瓷材料及其应用[M].北京:化学工业出版社,2005:16. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%