利用Gleeble1500热模拟试验机等试验设备,对挤压态AZ31镁合金进行预处理及高/恒应变速率下压缩超塑性研究.研究表明,挤压态镁合金在温度300℃,保温时间30 min为晶粒细化的较佳温度和保温时间,同时在300℃,应变速率为0.01～10 s-1的条件下进行压缩试验,外缘圆周伸长率均超过158.3%,压缩真应变达1.898以上,实现了高应变速率下的压缩超塑性.
参考文献
| [1] | Chang L I;Wang Y N;Zhao X et al.Microstructurro and mechannical properties in an AZ31 magnesium alloy sheet fab ricated by asymmetric hot extrusion[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2008,496:521-516. |
| [2] | 张佩武,夏伟,刘英,张卫文,陈维平.变形镁合金成形工艺研究及其应用[J].材料导报,2005(07):82-85. |
| [3] | Chuvil' deer V N;Nieh T G;Gryaznov M Yu et al.Superlasticity and internal friction in microcrystalline AZ91 and ZK60 magnesium alloys processed by equal-channel angular pressing[J].Journal of Alloys and Compounds,2004,378:253-257. |
| [4] | Watanabe H;Fukusumi M .Mechanical properties and texture of a superplastical deformed AZ31 magnesium alloy[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2008,477:153-161. |
| [5] | 郝艳君,陈立佳,吴伟.挤压态ZK60镁合金的高温力学性能及其超塑性[J].沈阳工业大学学报,2004(03):261-264. |
| [6] | 陈振华.变形镁合金[M].北京:化学工业出版社,2002:48-49,101-102. |
| [7] | 刘满平,马春江,王渠东,吴国华,朱燕萍,丁文江.工业态AZ31镁合金的超塑性变形行为[J].中国有色金属学报,2002(04):797-801. |
| [8] | 张诗昌,陈伟,韦中新,朱明.AZ31镁合金的超塑性研究[J].武汉科技大学学报(自然科学版),2008(05):547-551. |
| [9] | Wang Q F;Xiao X P;Hu J.An ultrafine-grained AZ31 magnesium alloy sheet with enhanced superplasticity prepared by aceumulative roll bonding[A].,2007:167-172. |
| [10] | 范钧,林飞.工业态AZ31镁合金超塑压缩试验研究[J].新技术新工艺,2007(01):54-56. |
| [11] | 黄蓓蓓,蔡庆伍,魏松波,丁睿,毛燕.AZ31镁合金热压缩变形行为分析[J].热加工工艺,2007(24):20-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%