根据光固化成型技术(SL)工艺对光敏树脂的要求和光敏树脂的固化机理,选择匹配的单体三羟甲基丙烷三丙烯酸酯和光引发剂2-异丙基硫杂蒽酮,通过大量的试验合成光敏树脂.针对研制的光敏树脂力学性能不太理想的问题,利用经表面处理后的SiC晶须对树脂体系进行增韧试验,晶须的表面处理工艺和晶须含量(含量均指质量分数)对光固化复合材料力学性能的影响、晶须含量对光固化复合材料固化速度的影响进行分析.实验结果表明:改性后的光敏树脂力学性能有所提高;随着晶须含量的增加,固化速度明显变慢.
According to the demand of stereolithograghy for photosensitive resins and the solidified mechanism of photosensitive resins, the matching monomer-TMPTA, photoiniator-ITX were selected, and the photosensitive resins were synthesized by lots of experiments. As the mechanical properties of the synthesized photosensitive resins were unsatisfied, photosensitive resins were toughened using surface treated SiC whisker, and effect of surface treatment techniques and mass fraction of SiC whisker on mechanical properties of light-cured composite material and effect of SiC whisker' mass fraction on curing rate of 1 ight-cured composite material were studied The result indicates that mechanical properties of modified photosensitive resins increase, and curing rate becomes slow with mass fraction of SiC whisker increasing.
参考文献
| [1] | 李武.无机晶须[M].北京:化学工业出版社,2005:5-100. |
| [2] | 靳治良,李胜利,李武.晶须增强体复合材料的性能与应用[J].盐湖研究,2003(04):57-66. |
| [3] | 王雪明,李爱菊,李国丽,王威强.金属表面KH-560硅烷膜的粘结性能研究[J].机械工程材料,2005(11):8-10,66. |
| [4] | 胡晓兰 .晶须改性热固性树脂的研究[D].西北工业大学,2002. |
| [5] | 杨媛丽,王永祯,王爱玲.光固化快速成型中光敏树脂固化机理研究[J].材料开发与应用,2006(06):8-10. |
| [6] | 曹玉军,刘杰.SiC晶须增韧WC陶瓷刀具材料的研究[J].硬质合金,2005(03):161-166. |
| [7] | 王晓丽,刘俊龙.紫外光固化环氧丙烯酸酯光敏预聚物改性研究进展[J].辽宁化工,2007(01):34-37. |
| [8] | 彭龙贵,王晓刚,杨晓凤,华小虎,曾志飞.β-型碳化硅晶须与颗粒的制备及特性表征[J].矿冶工程,2006(06):95-98. |
| [9] | 丁燕鸿,杨杨.SiC晶须/颗粒增韧金属陶瓷切削刀具的研究[J].株洲工学院学报,2006(04):60-62. |
| [10] | 闻荻江.复合材料原理[M].武汉:武汉工业大学出版社,1998:30-70. |
| [11] | 贾海涛,王永祯,王爱玲.光固化快速成型材料的合成及光聚合反应研究[J].材料导报,2006(12):132-133,143. |
| [12] | 刘长利,吴文健,满亚辉,张学骜,钱斯文.光固化有机硅/纳米SiO2杂化材料的制备和表征[J].材料科学与工程学报,2006(06):808-810,820. |
| [13] | 王永祯,贾海涛,杨媛丽,王爱玲.光固化快速成型中光敏树脂合成及其特性[J].中北大学学报,2006(05):400-404. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%