金属铜箔为反射层,以铁氧体吸波片为吸波层,分别与人造板复合,制成层状木基复合材料,研究该复合材料的电磁参数及其屏蔽效能和反射率随铁氧体含量的变化.结果表明,所制备的层状木基复合材料在频率小于500 MHz时平均为90 dB左右,当频率大于700MHz时,其屏蔽效能随着MnZn铁氧体含量的增加略有下降,在铁氧体的质量分数为80%时,其屏蔽效能为78dB左右,复合材料的反射率随着铁氧体吸收剂含量的增加,吸收峰带宽增加,在1.11 GHz处其反射率为-9.957dB,反射率小于-5dB的带宽范围在818 MHz～1.5 GHz.
The layered wood-based composite material was prepared by wood-based panel as based material,copper foil as shielding layer and MnZn ferrite sheet as absorbing layer,with epoxy resin as adhesives.The dielectric and magnetic parameters as well as shielding efficiency and reflectivity were investigated.The results showed that the shielding efficiency of the material was 90 dB with frequency less than 500 MHz.When the frequency was more than 700 MHz,the shielding efficiency decreased with the content of MnZn ferrite increasing.The reflectivity of the layered wood composite material was-9.57 dB with 80 wt% MnZn ferrite content at 1.11 GHz.The band width of reflectivity less than-5 dB was within 818 MHz～1.5 GHz.
参考文献
| [1] | 刘顺华;刘军民;董星龙.电磁波屏蔽及吸波材料[M].北京:化学工业出版社,2007 |
| [2] | 罗朝晖;朱家琪;黄泽恩 .木材/金属复合材料的研究[J].木材工业,2000,14(06):25-27. |
| [3] | 刘贤淼,傅峰.木基电磁屏蔽（导电）功能复合材料的研究进展[J].世界林业研究,2005(02):57-62. |
| [4] | Cao M;Wang B;Li Q et al.Towards an intelligent CAD system for multilayer electromagnetic absorber design[J].Materials & Design,1998,19(03):113-120. |
| [5] | 崔晓冬,刘顺华,管洪涛,李欣歌.双层吸波材料吸波特性研究[J].材料科学与工程学报,2006(05):725-729. |
| [6] | 吴行,饶大庆,谢宁,陈家钊,涂铭旌.多层复合型电磁屏蔽涂料的研究[J].功能材料,2001(04):365-367. |
| [7] | 居毅,杨元兆.高磁导率MnZn铁氧体的研究进展[J].浙江工业大学学报,2004(06):620-624. |
| [8] | 任慧,焦清介,康飞宇,崔庆忠,李江存.纳米铁氧体复合材料制备及吸波性能研究[J].稀有金属材料与工程,2007(z2):223-226. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%