针对攀钢实际,首次采用钒渣浸出钒液为原料,经除杂、水解沉淀和高温煅烧后制得VO2粉末.试验最佳条件为:除铬剂Z加入量与溶液中总铬量之比为22.86∶1;除硅剂X加入量与溶液中总硅量之比为3.2∶1;水解沉钒时溶液pH值控制在4.5～5.0之间;循环洗涤5次,煅烧温度1 000 ℃,恒温时间60 min,氩气流量4 L/min.与已有制备方法相比,该方法原料来源广泛,成本较低,工艺简单、适用,易于实现产业化.
参考文献
| [1] | Lawton SA.;Theby EA. .SYNTHESIS OF VANADIUM OXIDE POWDERS BY EVAPORATIVE DECOMPOSITION OF SOLUTIONS[J].Journal of the American Ceramic Society,1995(1):104-108. |
| [2] | Stanley A L;Edward A T .Effect of Tungsten and Molybdenum Doping on the Semiconductor-Metallic Transition in Vanadium Dioxide Produced by Evaporation Decomposition of Solutions and Hydrogen Reduction[J].Journal of the American Ceramic Society,1995,78:238-240. |
| [3] | 郑臣谋;张剑辉;张介立 等.纳米二氧化钒粉体的合成[J].中山大学学报(自然科学版),1999,38(06):54-56. |
| [4] | 雷德铭,何山,傅群,郑臣谋.VO2纳米粉体与纳米晶功能陶瓷的制备与特性[J].哈尔滨理工大学学报,2002(06):72-74. |
| [5] | 傅群,储向峰,林晨,雷德铭,郑臣谋.纳米VO2粉体的制备及性能特征[J].无机材料学报,2004(04):767-771. |
| [6] | Tsang C;Manthiram A .Sythesis of Nanocrystalline VO2 and its Electrochemical Behavior in Lithium Batteries[J].Electroche Soc,1997,144(02):520. |
| [7] | 尹大川;王猛;黄卫东 .纳米结构二氧化钒(VO2)的制备技术[J].西北工业大学学报,1999,17(03):493-495. |
| [8] | 朱小英;金德江 .V4+氧化物超微细粉的化学制备[J].中南民族学院学报(自然科学版),1997,16(03):23-27. |
| [9] | 徐时清,赵康,谷臣清.VO2 纳米粉末的无机溶胶-凝胶法合成及表征[J].稀有金属,2002(03):169-172. |
| [10] | 陈长琦,朱武,干蜀毅,方应翠,王先路.二氧化钒薄膜制备及其相变机理研究分析[J].真空科学与技术学报,2001(06):452-456. |
| [11] | 柏谈论;廖世明.国外钒冶金[M].北京:冶金工业出版社,1981:51. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%