通过水模实验优化水口结构形式和工艺参数,解决某钢厂165 mm×280 mm矩形坯连铸机在生产中出现的夹渣、鼓肚和粘结漏钢问题.优化范围包括水口的插入深度、出口倾角以及出口侧面和横断面的面积比.结果显示不同的水口形式对流场有不同的影响,目前使用的直通型水口正是造成生产中出现问题的症结所在.通过实验优化出适合165 mm×280 mm矩形坯的9#双侧孔水口和42#四孔水口.
参考文献
| [1] | 蔡开科;程士富.连续铸钢原理与工艺[M].北京:冶金工业出版社,1994:96-100. |
| [2] | Huang X;Thomas B G .Modeling of Transient Flow Phenomena in Continuous Casting of Steel[J].Canadian Metallurgical Quarterly,1998,37(03):197-212. |
| [3] | Ferretti A;Podrini M;Di Schino D.Submerged Nozzle Optimization to Improve Stainless Steel Surface Quality at Terni Steel Works[A].Iron & Steel Soc of AIME,1985:49-57. |
| [4] | Zhe WANG .Influence of Wettability on the Behavior of Argon Bubbles and Fluid flow inside the Nozzle and Mold[J].ISIJ International,1999(2):154-163. |
| [5] | Kim K .Analysis of Surface and Internal Cracks in Continuously Cast Beam Bleak[J].Ironmaking and Steelmaking,1997,24(03):249. |
| [6] | Jung-Eui Jong-Kyu Yoon .3-dimensional Mathematical Model for the Analysis of Continuous Beam Blank Casting Using Body Fitted Coordinate System[J].ISIJ International,1998(2):132-141. |
| [7] | 张乔英,王书桓,王立涛,朱立光,王硕明,周英超,徐学永,陆殿华.SEN壁厚对结晶器内钢液流场和温度场的影响[J].炼钢,2005(03):51-53. |
| [8] | 张先棹.冶金传输原理[M].北京:冶金工业出版社,1988:108-109. |
| [9] | 朱苗勇;刘家奇;肖泽强 .板坯连铸结晶器内钢液流动过程的模拟仿真[J].钢铁,1996,31(08):23-27. |
| [10] | 包燕平,田乃媛,徐保美.薄板坯连铸机新型浸入式水口[J].北京科技大学学报,2002(03):262-265. |
| [11] | 陈永范;陈德杰;李权 .大板坯连铸结晶器内流场实验研究[J].炼钢,1998,14(02):25-28. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%