为了快速、准确的研究高速电镀锌工艺,确定电解液流速、硫酸锌浓度和电流密度与电镀锌层表面质量的关系,采用白度颜色测定仪测定镀层表观明度值(L)的方法,评价高速电镀锌镀层的表面质量,同时利用明度法研究了在硫酸盐电解液中不同电流密度下的高速电镀锌工艺.研究结果表明:采用明度评价镀锌板表面质量的方法简单、方便,当镀层明度值L≥75时镀层均具有合格的外观,当L≥82时,镀层具有优良的外观;电流密度在50～150 A@dm-2区间时,在不同的硫酸锌浓度(250～350g/L)和高流速(3～4 m/s)下均能得到外观质量合格的镀锌层,而当电流密度为190 A@dm-2时,只有在高硫酸锌浓度(350～450g/L)和高流速(3～4 m/s)下时才能获得合格的镀层表面质量.
参考文献
| [1] | WEYMEERSCHA;WINAND R .Zinc electrodeposition at high current densities Part 1 : electrochemical study[J].Plating and Surface Finishing,1981,70(04):56-58. |
| [2] | WEYMEERSCHA;WINAND R .ZincelectrodepositionathighcurrentdensitiesPart2:characteristicsodeposits[J].Plating and Surface Finishing,1981,70(05):118-121. |
| [3] | WINANDR.Electrocrystailization: fundamental considerations and application to high current density continuous steel sheet plating[J].Journal of Applied Electrochemistry,1991(21):377-385. |
| [4] | LINDSAYJH .Electrogaivanized automotive sheet steel and the manufacturing system[J].Plating and Surface Finishing,1992,81(08):30-31. |
| [5] | 神田腾美 .家裂品用覆装板の向[J].表面技术,1996,47(07):33-35. |
| [6] | LASERMS;NOWAK E T .ThenewEGLatI/Nkoto[J].Plating and Surface Finishing,1994,183(01):13-15. |
| [7] | ROERTST;GUZZETTA F H .Morphology of high rate electrozinc[J].Plating and Surface Finishing,1988,77(09):53-55. |
| [8] | 中野博昭;荒贺邦康 .Znめつき皮膜の晶形,配向性に及ぼす解件の影[J].铁と,1997,83(12):13-16. |
| [9] | 鹭山胜;川边正 .めつき皮膜の表面粗さと结晶に及ぼす解件浴件の影[J].铁と,1990,76(08):1301-1305. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%