针对汽车工业急待解决的连杆腐蚀裂纹造成的减振器失效问题,对腐蚀裂纹建立了毛细管模型,试验研究了不同电流密度高效镀铬条件下减振器连杆镀层的微裂纹特征和腐蚀裂纹扩展规律.结果表明:电流密度为58 A/dm2时镀铬层微裂纹数量多且细密,在此电流密度下由于腐蚀电流的分散连杆基体的耐蚀性较好;镀铬层极化电流密度和裂纹长径比呈双曲线关系,电流密度为58 A/dm2时镀层腐蚀裂纹短而浅,耐腐蚀性能好.
参考文献
| [1] | 陈亚,苗艺,王春林.我国高效硬铬电镀技术的应用与发展[J].电镀与环保,2000(03):5-8. |
| [2] | NOBUHIRO Kuriyama;TETSUO Sakai .Characterization of metal hydride electrodes by means of electrochemical impedance spectroscopy[J].Journal of Alloys and Compounds,1993,192:161-163. |
| [3] | Gustavo C;NARASI S .Application accelerated corrosion test to service life prediction of materials[J].Journal of Electroanalytical Chemistry,1994,78(04):53-60. |
| [4] | EI-SHARIF M R;CHISHOLM C U;Su Y L .Corrosion Resistance of electrodeposited zinc-chromium alloy coatings[J].Corrosion Science,1993,35(05):259-265. |
| [5] | GILROY D;EDDOWS P J .Techniques for assessing the protective properties of chromate conversion coatings[J].Metal Finishing,1996,94(10):26-33. |
| [6] | 卢世刚.氢气在贮氢合金电极上析出反应机理的研究[J].电化学,1998(03):265. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%