为制备固相含量高、适合流延工艺的氧化铝陶瓷悬浮体,并保证成型坯片具有良好的强韧性能,通过分析陶瓷悬浮体的粘度、Zeta电位、接触角等参数,研究了各种添加剂对凝胶流延工艺的影响.实验结果表明:分散剂可提高悬浮体的Zeta电位,从而提高固相体积含量;增塑剂可明显提高坯片的柔韧性;表面活性剂可大幅度降低悬浮体与基带的接触角(从93°降低到72.2°).成功制备出固相含量超过50%的悬浮体,成型后的坯片表面平整,强度高,柔韧性好.
参考文献
| [1] | Mistler R E .Tapecasting:past, present, potential[J].American Ceramic Society Bulletin,1998,77(10):82-86. |
| [2] | Hotza D;GREIL P .Review:aqueous tape casting of ceramic powders[J].Materials Science and Engineering,1995,202:206-217. |
| [3] | Mistler R E .Tape Casting:the basic process for meeting the needs of the electronics industry[J].American Ceramic Society Bulletin,1990,69(06):1022-1026. |
| [4] | Chartier T;BRUNEAU A .Aqueous tape casting of alumina substrates[J].Journal of the European Ceramic Society,1993,12:243-247. |
| [5] | Doreau F;TARI G;PAGNOUX C et al.Processing of aqueous tape-casting of alumina with acrylic emulsion binders[J].Journal of the European Ceramic Society,1998,18:311-321. |
| [6] | Briscoe B J;BIUNDO G Lo;OZKAN N .Drying of aqueous eeramic suspensions[J].Key Engineering Materials,1997,132:354-357. |
| [7] | ANNIKA;KRISTOFFERSSON;CARLISTROM ELIS .Tape casting of alumina in water with an acrylic latex binder[J].Journal of the European Ceramic Society,1997,17:289-297. |
| [8] | PAGNOUX C;CHARTIER T .Aqueous suspensions for tape-casting based on acrylic binders[J].Journal of the European Ceramic Society,1998,18:241-247. |
| [9] | Rodrigo Moreno .The role of slip additives in tapecasting technology:Part I-solvents and dispersants[J].American Ceramic Society Bulletin,1992,71(10):1521-1531. |
| [10] | Rodrigo Moreno .The role of slip additives in tape-casting technology:Part Ⅱ-binders and plasticizers[J].American Ceramic Society Bulletin,1992,71(11):1647-1657. |
| [11] | 郑忠;胡纪华.表面活性剂的物理化学原理[M].广州:华南理工大学出版社,1995 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%