采用自蔓延高温合成(SHS)工艺制备了Ni0.25Cu0.25Zn0.5Fe1.96O3.94粉体,将铁氧体粉体分别在800、850、900℃进行热处理,以XRD、SEM、TG-DSC、振动样品磁强计(VSM)等手段分别对产物的物相、微观结构和磁性能进行研究.结果表明,SHS制备的NiCuZn铁氧体粉体经900℃热处理后可以转变成单一的尖晶石相,所得铁氧体粉体结构完整,矫顽力达到最小值,Hc=5 753.417 1A/m,同时饱和磁化强度达到最大值,Ms=68.34 emu/g.
参考文献
| [1] | Yen-Pei Fu;Ko-Yin Pan;Cheng-Hsiung Lin .Microwave-induced combustion synthesis of Ni_(0.25)Cu_(0.25)Zn_(0.5) ferrite powders and their characterizations[J].Materials Letters,2002(2):291-296. |
| [2] | 何新华,熊茂仁,凌志远,丘其春.多层片式电感器用 NiCuZn铁氧体的低温烧结[J].无机材料学报,1999(01):71-77. |
| [3] | 凌志远;熊茂仁;丘其春 等.高性能低温烧结NiCuZn铁氧体μ125材料的研究[J].磁性材料及器件,1997,29(01):1-5. |
| [4] | Darko Makovec;Miha Drofenik;Andrej Znidarsic .Hydrothermal synthesis of manganese zinc ferrite powders from oxides[J].Journal of the American Ceramic Society,1999(5):1113-1120. |
| [5] | Chen C J;BRIDGET K .A novel low-temperature preparation of Ni-Zn ferrite and the properties of the ultrafine particles formed[J].Journal of Applied Physics,1988,63(08):3786-3789. |
| [6] | 徐强,张幸红,赫晓东,韩杰才,王雪峰.TiB2-Cu复合材料SHS工艺的人工神经网络优化[J].哈尔滨工业大学学报,2003(10):1199-1201. |
| [7] | 朱春城,赫晓东,曲伟.SHS工艺制备TiC-TiB2/Cu-Ni复合材料的性能[J].哈尔滨工业大学学报,2003(08):953-957. |
| [8] | 李垚,赵九蓬,韩杰才,杜善义.自蔓延高温合成Ni0.35Zn0.65Fe2O4粉体的研究[J].硅酸盐学报,2000(05):427-431. |
| [9] | 赵九蓬,李垚,赫晓东,韩杰才,杜善义.自蔓延高温合成Ni-Zn铁氧体反应机制的研究[J].硅酸盐学报,2002(01):9-13. |
| [10] | 李垚,赵九蓬,韩杰才,赫晓东,杜善义.铁氧体粉料制备工艺的新进展[J].粉末冶金技术,2000(01):51-55. |
| [11] | 姜久兴,李垚,赫晓东,曲伟.ZnFe2O4粉体的燃烧合成[J].硅酸盐学报,2003(03):235-240,249. |
| [12] | 姜久兴,李垚,赫晓东,曲伟,李晓.MnZn铁氧体粉体的燃烧合成[J].哈尔滨工业大学学报,2004(01):11-15. |
| [13] | 李垚,赵九蓬,姜久兴,赫晓东.燃烧合成ZnFe2O4的相转变与反应机制研究[J].材料科学与工艺,2004(01):41-44. |
| [14] | 姜久兴,李垚,赫晓东,曲伟.MnFe2O4粉体的燃烧合成[J].粉末冶金技术,2003(05):264-269. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%