为了阐明EAF-LF-CSP工艺生产的低碳钢组织细化机理,在薄板坯和不同道次变形后的同一轧件上取样,利用金相、SEM、TEM、XEDS等技术研究了连轧过程中显微组织演变和钢中第二相析出物.结果表明:与普通连铸板坯相比薄板坯的凝固组织更加细小;随轧制道次增加,薄板坯表面和心部的组织差异逐渐减小,轧后室温组织细化;CSP生产的低碳钢中存在大量纳米尺寸的氧化物和硫化物,起到细化晶粒的作用.CSP生产中采用快速冷却和凝固工艺、单道次大压下连轧工艺和层流冷却工艺,是成品组织细化的主要原因.
参考文献
| [1] | S. J. Cobo;C. M. Sellars .Microstructural evolution of austenite under conditions simulating thin slab casting and hot direct rolling[J].Ironmaking & Steelmaking: Products and applications,2001(3):230-236. |
| [2] | ZENTARAN;KASPER R .OptimizationofhotrollingschedulefordirectchargingofthinslabsofNb-Vmicroalloyedsteel[J].Materials Science and Technology,1994,10:370-376. |
| [3] | RIMACOMEJK;SAMARASEKERA I V .Thechallengeofthinslabcasting[J].Ironmaking and Steelmaking,1994,21(11):29-39. |
| [4] | KASPERR;ZENTARA N;HERMAN J C .Direct charging of thin slabs of a Ti-microalloyed low carbon steel for cold forming[J].Steel Research International,1994,65(07):279-283. |
| [5] | P.C. Zambrano;M.P. Guerrero;R. Colas .Microstructural analysis of hot-rolled, low-carbon steel strips[J].Materials Characterization,2001(3/4):275-282. |
| [6] | FLEMMINGG;HOFFMAN F;ROHDE W et al.The CSP plant technology and its adaptation to an expanded production progranmme[J].Metallurgical Plant and Technology International,1993,16(02):84-96. |
| [7] | Delu Liu,Jie FU,Yonglin KANG,Xiangdong Huo,Yuanli Wang,Nanjing Chen,Zhongbing Wang,Liejun Li.Oxide and Sulfide Dispersive Precipitation and Effects on Microstructure and Properties of Low Carbon Steels[J].材料科学技术学报(英文版),2002(01):7-9. |
| [8] | Delu Liu,Xiangdong Huo,Yuanli Wang.Oxide and Sulfide Dispersive Precipitation in Ultra-low Carbon Steels[J].北京科技大学学报(英文版),2001(04):314. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%