研究了Ti-V-Nb微合金钢及热影响区(HAZ)第二相粒子及其对HAZ区奥氏体晶粒长大的影响.结果表明,微合金钢中存在大量弥散分布、细小粒子的Ti、Nb、V的碳氮化合物.这些具有很高的稳定性,在焊接热循环过程中,显著地阻止奥氏体晶粒长大.焊接热循环峰值温度在1200℃以下时,HAZ区中第二相粒子仅发生轻微的溶解及长大,奥氏体晶粒长大程度很小,且奥氏体晶粒尺寸基本不随ts/5及热循环峰值温度Tm的变化而变化.焊接热循环峰值温度在1250℃以上时,HAZ区中第二相粒子显著减少而尺寸显著增大,奥氏体晶粒尺寸随t8/5及Tm的增大而显著增大.
参考文献
| [1] | MUSTSUO N;YUICHI K .ImprovementofweldedHAZToughnessbydispersionwithnitrideparticlesandoxideparticles[J].Journal of the Japan Welding Society,1983,52:117-131. |
| [2] | Strid J;EASTERLING K E .Onthechemistryandstabilityofcomplexcarbideandnitridesinmicroalloyedsteels[J].Acta Metallurgy,1985,33:2057-2074. |
| [3] | LOGERG B;EASTERLING K E .TheroleofalloycompositiononstabilityofnitrideinTimicroalloyedsteelduringweldthermalcycling[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1984,15:33-40. |
| [4] | ADRAIN H;PICKERING F B .EffectofTiadditiononaustenitegraingrowthkineticsofmediumcarbonV-Nbsteelscontaining0.008-0.18%N[J].Materials Science and Technology,1991,7(02):176-182. |
| [5] | 雍岐龙;马鸣图;吴宝榕.微合金钢[M].北京:机械工业出版社,1989 |
| [6] | 陈茂爱,孙文涛,唐逸民,楼松年,吴人洁.焊接热循环对Ti-V-Nb微合金钢中第二相粒子的影响[J].机械工程学报,2000(10):99. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%