为减少熔炼时合金元素的烧损,采用真空感应熔炼工艺制备了低铬铜铬合金.通过扫描电镜、光学显微镜和能谱分析等手段,研究了真空环境下不同浇注工艺对合金铸锭组织、缩孔及成分偏析的影响.研究结果表明:利用真空直接加铬炼制低铬铜铬合金,采用合适的熔炼和浇注工艺,可以较精确控制合金成分;在低的浇注温度和大冷却速度下可以获得几乎无宏观偏析,铸造缺陷很少的铜铬合金铸件;铸件500℃退火3 h后,硬度可达141HV,电导率提高到86%IACS.
参考文献
| [1] | 田荣璋;王祝堂.铜合金及其加工手册[M].长沙:中南大学出版社,2002 |
| [2] | Turkin AA.;Bakai AS.;Abromeit C.;Naundorf V.;Wanderka N.;Turkin YA. .MODELLING OF CASCADE-INDUCED DISSOLUTION OF COHERENT CHROMIUM PRECIPITATES IN COPPER[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,1995(2):143-150. |
| [3] | R. D. K. Misra;V. Satya Prasad;P. Rama Rao .Dynamic embrittlement in an age-hardenable copper-chromium alloy[J].Scripta materialia,1996(1):129-133. |
| [4] | T. FUJII;H. NAKAZAWA;M. KATO .CRYSTALLOGRAPHY AND MORPHOLOGY OF NANOSIZED Cr PARTICLES IN A Cu-0.2 Cr ALLOY[J].Acta materialia,2000(5):1033-1045. |
| [5] | Gao N;Huttunen-Saarivirta E;Tiainen T et al.Influence of prior deformation on the age hardening of a phosphorus containing Cu-0.61wt.% alloy[J].Materials Science and Engineering,2003,A342:270-278. |
| [6] | 冼爱平.大功率真空开关铜铬触头材料[J].中国有色金属学报,2001(05):731-740. |
| [7] | 刘京雷,刘祖岩,王尔德.机械球磨Cu-15%Cr复合粉末的致密化工艺研究[J].材料科学与工艺,2003(02):136-139. |
| [8] | 孔庆祥.铜铬合金直接加铬熔炼和铸造[J].材料开发与应用,1997(04):38. |
| [9] | 马凤仓,倪锋,杨涤心.高铬含量铜铬合金的真空熔炼[J].材料开发与应用,2003(01):8-11. |
| [10] | 陈存中.有色金属熔炼与铸锭[M].北京:冶金工业出版社,1999 |
| [11] | 戴永年;杨斌.有色金属材料的真空冶金[M].北京:冶金工业出版社,2000 |
| [12] | 周尧和;胡壮麟;介万奇.凝固技术[M].北京:机械工业出版社,1998 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%