采用了11种实验室模拟工艺(650～750 ℃、1.5～873 h),利用TEM、SEM、OM等考察了珠光体耐热钢12Cr1MoV高温长时间加热后成分、组织结构与性能的变化.研究表明,试验用钢在高温时效后其组织结构明显退化,固溶体内合金元素Cr、Mo、V严重贫化(其中Mo的降幅为2/3),发生晶粒长大(～70%),碳化物向晶界的聚集粗化,以及相变位错密度显著降低和位错胞尺寸变大及消散等,同时基体硬度下降30%.多层次结构综合分析表明,12Cr1MoV耐热钢高温时效中,由于组织结构的退化,引起其性能的劣化,导致材料的弱化(老化).
参考文献
| [1] | National Research Council.Materials Science and Engineering for the 1990s[M].Washigon,D.C:National Academy Press,1990 |
| [2] | 杨瑞成;邓文怀;冯辉霞.工程设计中的材料选择与应用[M].北京:化学工业出版社,2004 |
| [3] | INDACOCHEA J E .An analysis of creep damage in a welded low alloy steel rotor[J].Materials Science and Engineering A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,1997,234-236:555. |
| [4] | JOARDER A .Effects of long-term service exposure on microstructure and properties of a Cr-Mo-V steam turbine rotor steel[J].Metallurgical Transactions,1991,22A(08):1811-1820. |
| [5] | SENIOR B A .A critical review of precipitation behavior in Cr-Mo-V rotor steel[J].Science and Engineering A,1988,103(02):263-272. |
| [6] | CHERU N B .Degradation of mechanical properties of Cr-Mo-V and 2.25Cr-1Mo steel components after longterm service at elevated temperatures[J].Metallurgical Transactions,1989,20A(01):87-97. |
| [7] | 杨玉玥;李志文 .Q法预测12Cr1MoV钢主蒸汽管道剩余寿命[J].金属学报,1999,35(07):721-725. |
| [8] | 杨瑞成,王晖,羊海棠,陈奎,袁晓波.用Larson-Miller参数描述12Cr1MoV与 15CrMo的老化行为[J].材料科学与工艺,2002(04):395-398. |
| [9] | 杨瑞成,王晖,刘忠艳,史亚春.珠光体耐热钢Larson-Miller参数的确定与验证[J].甘肃工业大学学报,2002(03):23-26. |
| [10] | 杨瑞成,傅公维,王凯旋,王晖.15CrMo耐热钢Larson-Miller参数值的确定与应用[J].兰州理工大学学报,2004(03):27-30. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%