以短切高模炭纤维为增强体.制备C/C复合材料,并采用XRD、SEM等方法研究了纤维体积含量和石墨化度对复合材料性能的影响.结果表明:当短切高模炭纤维体积含量小于7%时,随着炭纤维体积含量增加,C/C复合材料的力学性能逐渐升高,高于7%时力学性能降低;随着石墨化度提高,C/C复合材料的力学性能显著降低,短切高模炭纤维增强作用下降;C/C复合材料的石墨化度对电阻率影响大,纤维体积含量对电阻率几乎没有影响;C/C复合材料的石墨化度对材料的抗氧化性影响显著.
参考文献
| [1] | 赵宗桂.碳纤维及其复合材料的发展与应用[J].石化技术与应用,2002(04):273-276. |
| [2] | 赵稼祥.美国HEXEL公司的碳纤维及其复合材料[J].热固性树脂,2001(03):44-48. |
| [3] | Dibiasova L.;Stary V.;Glogar P. .Analysis of carbon fibers and carbon composites by asymmetric X-ray diffraction technique[J].Carbon: An International Journal Sponsored by the American Carbon Society,1999(3):421-425. |
| [4] | CHO Donghwan;YOON Byung Ⅱ .Microstructural interpretation of the effect of various matrices on the ablation properties of carbon-fiber-reinforced composites[J].Composites Science and Technology,2001,61:271-280. |
| [5] | 冯志荣,黄启忠,邹林华.石墨化度对C/C复合材料摩擦性能的影响[J].粉末冶金工业,2000(03):29-32. |
| [6] | Zou LH.;Huang BY.;Huang Y.;Huang QH.;Wang CA. .An investigation of heterogeneity of the degree of graphitization in carbon-carbon composites[J].Materials Chemistry and Physics,2003(3):654-662. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%