摩擦压扭强变形区热诱导转移法是一种制备棒状超细晶材料的新方法.为深入研究晶粒细化过程的热力学参数,采用传热学理论,分别建立了试验过程中母材区、变形区和细晶区沿试样轴向的温度分布数学模型,讨论了加热功率、冷却程度及材料物理参数对温度分布的影响.研究表明:变形区温度随输入功率的增加而增加,而随变形区转移速度和冷却程度的增大而迅速降低;母材区温度梯度远大于细晶区温度梯度;输入功率对变形区及细晶区温度影响较大,散温系数对细晶区温度下降梯度影响大.直径11 mm的1Cr18Ni9Ti不锈钢晶粒细化过程中变形区温度约为944 ℃.
参考文献
| [1] | GERTSMAN V R .On the structure and strength of ultrafine-grained copper produced by severe plastic deformation[J].Scripta Metallurgical and Mechanical,1994,30:229-234. |
| [2] | Terry C. Lowe;Ruslan Z. Valiev .The Use of Severe Plastic Deformation Techniques in Grain Refinement[J].JOM,2004(10):64-68. |
| [3] | TSUJI N;IWATA T;SATO M et al.Aging behavior of uhrafine grained Al-2 wt%Cu alloy severely deformed by accumulative roll bonding[J].Science and Technology of Advanced Materials,2004,5(1-2):173-180. |
| [4] | H.K. Kim;W.J. Kim .Microstructural instability and strength of an AZ31 Mg alloy after severe plastic deformation[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):300-308. |
| [5] | 杜随更,王彦绒.超细晶材料制备的摩擦压扭强变形区转移法[C].2002年材料科学与工程新进展（2002年中国材料研讨会：论文专辑）,2002:248-251. |
| [6] | CHAPMAN A J;何用梅.传热学[M].北京:冶金工业出版社,1984 |
| [7] | ПОЛУКИНП Н;林治平.金属与合金的塑性变形抗力(手册)[M].北京:机械工业出版社,1984 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%