为优化电沉积制备软磁铁箔的工艺条件,研究电解液温度和阴极电流密度对铁箔的磁学、力学和电学性能的影响规律,采用软磁材料测试仪、直流电阻电桥和显微硬度计研究了工艺条件变化时对铁箔的磁参数、电阻率和显微硬度的影响,并对铁箔的金相显微组织进行分析.结果表明:阴极电流密度增大时,铁箔的矫顽力增大,最大磁导率降低,显微硬度值及电阻率均提高;电解液温度提高时,铁箔的矫顽力降低,最大磁导率增大,显微硬度值下降,而电阻率提高;在650 ℃经过真空退火后的铁箔矫顽力降低,最大磁导率提高,其电阻率和硬度都下降,韧性明显提高.电沉积工艺条件改变时,薄膜的晶粒尺寸影响铁箔性能的变化.
参考文献
| [1] | MCGEOUGH J A;THOMSON J R .Some effects of electrolyte flow in the electroforming of iron foil[J].Proceedings of the Institution of Mechanical Engineers Part C Journal of Mechanical Engineering Science,1986,200(C2):111-122. |
| [2] | LI D Y;SZPUNAR J A .Texture formation mechanism during electrodeposition[J].Journal of Materials Science,1993,28(20):5554-5559. |
| [3] | Jean-Crahay;Nicole Lambert;Mario Economopoulos .Elofoil, a new process for the production of iron foil[J].Metallurgical Plant and Technology International,1995(3):72-74,76-0. |
| [4] | 郭占成,刘宇星,刘美凤,卢维昌.电沉积Fe、Ni基合金箔的组织形貌及磁性能[J].中国有色金属学报,2004(02):273-279. |
| [5] | 姜力强,郑精武,陈巧玲.电沉积软磁铁箔连续化生产的关键技术研究[J].稀有金属,2005(03):293-296. |
| [6] | 徐永兰,卢维昌,王中礼.电解成型铁箔的结晶形态[J].化工冶金,1989(01):1-7. |
| [7] | 田民波.磁性材料[M].北京:清华大学出版社,2000 |
| [8] | 杨防祖.添加剂的吸附行为及其对锌镍合金镀层结构的影响[J].厦门大学学报,1995(04):572. |
| [9] | 王晓平,赵特秀,季航,梁齐,董翊.晶粒尺寸对薄膜电阻率温度系数的影响[J].物理学报,1994(02):297-302. |
| [10] | 宗影影,薛克敏,单德彬,吕炎.热处理对BT14钛合金显微组织和力学性能的影响[J].材料科学与工艺,2004(05):546-548. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%