采用固相烧结法分别制备了钴掺杂和镍掺杂锰酸锂锂离子电池正极材料,同时制备了纯相锰酸锂进行比较.用电感耦合等离子发射光谱仪、X射线衍射仪、电子扫描电镜和电池性能测试系统对产物的组成、结构特征、微观表面形貌和恒流充放电性能进行了表征.结果表明:所制备的掺杂锰酸锂LiMn0.9Ni0.1O2、LiMn0.9Co0.1O2的结晶度高,无杂质相,材料颗粒的粒径均匀、表面光滑;首次放电比容量分别为114.7 mAh/g和110.8 mAh/g(0.5 mA/cm,2.8～4.4 V,vs.Li+/Li);50次循环后,放电比容量为107.2 mAh/g和103.3 mAh/g,50次循环比容量保持率分别达到94.1%和95.4%.
参考文献
| [1] | FEY G T K;R SHIU F;CHEN J G.LiNi0.8Co0.2O2 cathode materials synthesizod by the maleic acid assisted sol-gel method for lithium batteries[J].Journal of Power Sources,2002(103):265-272. |
| [2] | 雷太鸣,周新文,宗红星,张克立.正交结构LixMnO2正极材料的合成及其电化学性能研究[J].无机化学学报,2005(02):261-264. |
| [3] | M. R. Wagner;P. R. Raimann;A. Trifonova;K.-C. Moller;J. O. Besenhard;M. Winter .Dilatometric and mass spectrometric investigations on lithium ion battery anode materials[J].Analytical and bioanalytical chemistry,2004(2):272-276. |
| [4] | LEE HY;BAEK JK;LEE SM et al.Effect of carbon coating on elevated temperature performance of graphite as lithium-ion battery anode material[J].Journal of Power Sources,2004,128(01):61-66. |
| [5] | 刘恒,孙红刚,周大利,张萍,尹光福.改进的固相法制备磷酸铁锂电池材料[J].四川大学学报(工程科学版),2004(04):74-77. |
| [6] | Thackeray MM. .STRUCTURAL CONSIDERATIONS OF LAYERED AND SPINEL LITHIATED OXIDES FOR LITHIUM ION BATTERIES[J].Journal of the Electrochemical Society,1995(8):2558-2563. |
| [7] | 何向明,王莉,张国昀,姜长印,万春荣.溶胶凝胶法合成锂离子电池正极材料LiMn2O4[J].电化学,2006(01):104-106. |
| [8] | 赵铭姝,翟玉春,田彦文.固相分段法制备锂离子电池正极材料L i Mn2O4的实验[J].过程工程学报,2001(04):402-407. |
| [9] | 李智敏,仇卫华,胡环宇,赵海雷,高长贺.锂离子电池正极材料锰酸锂的优化合成[J].无机材料学报,2004(02):342-348. |
| [10] | 唐新村,杨幼平,李立清,贾殿赠,黄可龙.LiMn2L（Ac）2热分解制备的尖晶石LiMn2O4及其电化学性能[J].中国有色金属学报,2004(05):871-876. |
| [11] | 唐致远,邓艳波,张娜,管道安.LiCoO2对LiMn2-xMxO4正极材料的混合改性研究[J].化学通报（印刷版）,2006(04):287-289. |
| [12] | 顾大明,张若楠,高农.尖晶石型锰酸锂制备及其电化学性能[J].哈尔滨工业大学学报,2008(04):607-610. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%