利用交流阻抗(EIS)、线性极化、动电位极化和失重法,研究了炔氧甲基季胺盐对N80在常温CO2饱和的3%NaCl溶液中的电化学行为和缓蚀性能的影响.结果表明:空白溶液中N80的累计失重在4 m/s以后急剧增大,即介质的临界流速为4～5 m/s.动态下炔氧甲基季胺盐存在与静态下相同的浓度极值现象,流速低于5 m/s时缓蚀剂的极值浓度与静态时相同,都为150 mg/L,而流速高于5 m/s后极值浓度有所增加.
参考文献
| [1] | 郭兴蓬,付朝阳.缓蚀剂和CO<,2>腐蚀产物膜的相互作用[C].第十二届全国缓蚀剂学术讨论会论文集,2001:7-12. |
| [2] | Dougherty J A;Stergmann D W .The effects of flow on corrosion inhibitors performance[J].Materials Performance,1996,35(04):47-53. |
| [3] | 刘小武,彭芳明,俞敦义,刘烈炜,郑家,刘志刚,王富才.输油管线缓蚀剂的研究[J].材料保护,2000(08):3-5. |
| [4] | Chen Y;Jepson W P.EIS measurement for corrosion monitoring under multiphase flow condition[J].Electrochimica Acta,1999(44):4453-4464. |
| [5] | Wang H B;Hong T;Jepson W P.Characterization of inhibitor and corrosion product film using electrochemical impedance spectroscopy(EIS)[J].Corrosion,2001:01023. |
| [6] | Smart J S.The meaning of the API - RP- 14 - E formula for erosion corrosion in oil and gas production[J].Corrosion,1991:468. |
| [7] | 蒋秀,骆素珍,郑玉贵,柯伟.炔氧甲基季胺盐和咪唑啉对N80在饱和CO2的3%NaCl溶液中的缓蚀性能研究[J].中国腐蚀与防护学报,2004(01):10-15. |
| [8] | 王佳;曹楚南 .缓蚀剂阳极脱附现象的研究-Ⅱ缓蚀剂阳极脱附对电极阻抗的影响[J].中国腐蚀与防护学报,1995,15(04):247-253. |
| [9] | 杨帆;郑玉贵;姚治铭;柯伟 .铜镍合金BFe30-1-1在流动人工海水中的腐蚀行为[J].中国腐蚀与防护学报,1999,19(04):207-213. |
| [10] | 曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994:328-344. |
| [11] | Malik H .Influence of C16 quaternary amine on surface films and polarization resistance of mild steel in carbon dioxide - saturated5% sodium chloride[J].Corrosion,1995,51(04):321-328. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%