用原位化学气相沉积方法在Cr17Ni2钢表面共渗铬硅,通过工艺优化,获得了含铬27wt%、含硅2wt%左右的渗层,渗层厚度约为120μm,渗层为单相的α固溶体.共渗后的热处理工艺对渗后材料的力学性能有较大的影响.
参考文献
| [1] | Bianco R;Harper M A;Rapp R A .Codeposition elements by halide-activated pack cementation[J].Journal of The Minerals,Metals & Materials Society,1991,43(11):68-73. |
| [2] | Harper M A;Miller D M;Rapp R A.Codeposition of chromium-silicon and chromium-aluminum in diffusion coatings for iron-base alloys using pack cementation[A].,1990:311-320. |
| [3] | Harper M A;Rapp R A .Chromized/siliconized diffusion coatings for iron-base alloys by pack cementation[J].Materials Performance,1991,30(09):41-44. |
| [4] | 万如;郭伟明 .不锈钢上的铬硅原位化学气相沉积[J].航空制造工程,1996,164(08):25-27. |
| [5] | 万如;白真权 .超高强度钢Cr-Si原位CVD及耐蚀性研究[J].中国腐蚀与防护学报,1997,17:494-497. |
| [6] | 科洛梅采夫ПГ;马志春.耐热扩散涂层[M].北京:国防工业出版社,1988 |
| [7] | Harper M A .Codeportion of chromium and silicon onto iron-base alloys via pack cementation[D].Ohio State University,1992. |
| [8] | 陈得和.不锈钢的性能与组织[M].北京:力学工业出版社,1977 |
| [9] | 刘宁 .Cr17Ni2钢高温回火脆性的初步研究[J].理化检验-物理分册,1987,23(01):3-6. |
| [10] | 刘宁.550℃去应力回火对Cr17Ni2钢性能的影响规律的初步研究[J].热加工工艺,1987(05):9. |
| [11] | 侯文泰 .Cr17Ni2不锈钢的相变及热处理对力学性能的影响[J].金属热处理,1980,4:26-35. |
| [12] | 中国航空材料手册编辑委员会.航空材料手册[M].北京:中国标准出版社 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%