对[001]取向单晶镍基合金恒载拉伸蠕变的组织形貌进行SEM观察和EDAX成分分析,研究了γ′相定向粗化特征及影响因素.结果表明,由于应力场和温度场的差别,蠕变样品不同位置处筏状γ′相粗化尺寸及特征不同,近断口处筏状γ′相扭曲且粗化加剧,随离断口距离增加,γ′相粗化程度减弱;在γ′相定向粗化的扩散场中,分配比值较小且相对稳定的元素W可成为其他元素的扩散障碍,使合金2中γ′相的形筏时间明显延长.
参考文献
| [1] | TIEN T K;COPLEY S M .The effect of uniaxial stress on the periodic morphology of coherent gamma prime precipitates in nickel-base superalloy crystals[J].Metallurgical and Materials Transactions,1971,2:215. |
| [2] | POLLOCK T M;ARGON A S .Directional coarsening in nickel-base single crystals with high volume fractions of coherent precipitates[J].Acta Metallurgica Et Materialia,1994,42(06):1859. |
| [3] | 彭志方;GLATZEL U;FELLER-KNIEPMEIER M .一种镍基单晶高温合金中γ′沉淀的定向粗化[J].金属学报,1995,31(12):A531. |
| [4] | 田素贵;张静华;杨洪才 等.一种单晶镍基合金蠕变期间γ′相的定向粗化机制[J].金属学报,1998,34(06):591. |
| [5] | 田素贵.单晶镍基合金稳态蠕变期间的内应力及影响因素[J].航空材料学报,1998(03):16. |
| [6] | SVETLOV I L;GOLOVKO B A;EPISHIN A I et al.Diffusional mechanism of γ′- phase particles coalescence in single crystals of nickel-base superalloys[J].Scripta Metallurgica et Materialia,1992,26:1353. |
| [7] | HILLERT MATS;赖和怡;刘国勋.合金扩散和热力学[M].北京:冶金工业出版社,1984:284. |
| [8] | 秦高梧;郝士明 .Ti-Al-Ga系及Ti-Al-Nb-Cr系α(α2)/γ相平衡研究[J].金属学报,1995,31(11):B485. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%