对两种热处理状态的Ti-6Al-4V锻件钛合金的疲劳小裂纹扩展行为进行了研究.使用应力强度因子范围ΔK对小裂纹和长裂纹的扩展速率进行关联.结果表明,恒幅载荷R=0和R=-1下两种材料都表现出小裂纹效应,R=-1下的小裂纹效应尤为明显.在相同应力比下对两种状态材料的小裂纹效应进行对比发现,应力比R=-1下,两种状态材料的小裂纹扩展行为非常相似.应力比R=0下,片层宽度较小的材料表现出的小裂纹效应较明显.
参考文献
| [1] | SURESH S;RITCHIE R O .Propagation of short fatigue cracks[J].International Materials Reviews,1984,29(06):445-475. |
| [2] | 吴学仁;NEWMAN J C.高强度铝合金的小裂纹效应[A].北京:航空工业出版社,1994 |
| [3] | DEMULSANT X;MENDEZ J .Microstructural effects on small fatigue crack initiation and growth in Ti6Al4V alloys[J].Fatigue & Fracture of Engineering Material & Structure,1995,18(12):1483-1497. |
| [4] | Lutjering G. .Influence of processing on microstructure and mechanical properties of (alpha+beta) titanium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):32-45. |
| [5] | LUTJERING G;GYSLER A;ALBRECHT J.Influence of microstructure on fatigue resistance[A].EMAS,1996:893-904. |
| [6] | BOLINGBROKE R K;KING J E;RITCHIE R O;LANKFORD J .The growth of short fatigue cracks in titanium alloys IMI 550 and IMI 318' small fatigue cracks[Z].,1986. |
| [7] | BROWN C W;HICKS M A.A study of short fatigue crack growth behaviour in titanium alloy IMI 685[J].Fatigue Engineering Material Structure,1982(06):67-74. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%