开展了Al2O3/YAG共晶自生复合陶瓷的激光熔凝制备技术的实验研究,研究结果表明:(1)激光扫描速率与功率密度的匹配对激光熔凝实验起着决定性的作用.调整工艺参数,可以获得表面光滑、平整、致密的熔凝层,且无宏观孔隙及裂纹.随扫描速率的增大,熔凝层变薄;(2)激光熔凝Al2O3/YAG共晶自生复合陶瓷由Al2O3相和YAG相两相组成,具有典型的快凝层状共晶组织,共晶间距非常细小.
参考文献
| [1] | 张军;李建国;傅恒志 .单晶高温合金高梯度定向凝固特性的比较研究[J].金属学报,1999,35:S220-224. |
| [2] | Waku Y.;Ohtsubo H.;Mitani A.;Shimizu K.;Nakagawa N. .Fracture and deformation behaviour of melt growth composites at very high temperatures[J].Journal of Materials Science,2001(7):1585-1594. |
| [3] | STUBICAN V S;BRADT R C .Eutectic solidification in ceramic systems[J].Annual Review of Materials Science,1981,11(04):267. |
| [4] | VIECHNICKI D;SCHMID F.Eutectic solidification in the system Al2O3/Y3Al5O12[J].Journal of Materials Science,1969(04):84. |
| [5] | W 库兹;P R 萨姆.定向凝固共晶材料[M].北京:冶金工业出版社,1989 |
| [6] | Orera V M;MERINO R I;PARDO J A et al.Microstructure and physical properties of some oxide eutectic composites processed by directional solidification[J].Acta Materialia,2000,48:4683. |
| [7] | Waku Y.;Sakata S.;Mitani A.;Shimizu K.;Hasebe M. .Temperature dependence of flexural strength and microstructure of Al2O3/Y3Al5O12/ZrO2 ternary melt growth composites[J].Journal of Materials Science,2002(14):2975-2982. |
| [8] | YU Jin-jiang;ZHANG Jun;WANG Feng et al.Microstructure evolution of Ni, Cr, Al-TaC in situ composite directionally solidified under high temperature gradient[J].Materials Science and Engineering,2001,311:200-204. |
| [9] | 杨森,黄卫东,刘文今,苏云鹏,周尧和.激光超高温度梯度快速定向凝固研究[J].中国激光,2002(05):475-479. |
| [10] | 张克丛;张乐惠.晶体生长科学与技术[M].北京:科学出版社,1997 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%