通过流变实验分析了滑石含量及球磨工艺对水基氧化铝陶瓷料浆流变性的影响.结果表明:滑石含量为0至4wt%时,随着滑石含量的增加,氧化铝料浆的静态粘度略有增大,且含有滑石的氧化铝料浆表现出明显的触变性;特定滑石含量(0.5wt%)的氧化铝料浆(体浓度55vol%)球磨时间为16～18h时,粘度达到最小值,流动性最好.
参考文献
| [1] | Mark A;JANNEY;OGBEMI O .OMETETE[P].Gelcasting of ceramic powders.U S Patent:5145908,1992. |
| [2] | OMETETE O O;MARK A JANNEY;STREHLOW R A .Gelcasting-a new ceramic forming process[J].Ceramic Bulletin,1991,70(10):1641-1649. |
| [3] | Mark A;JANNEY .Method for molding ceramic powders[P].US:4894194,1990. |
| [4] | Lange;FREDERICK F .VALAMAKANNI,BHASKER V.Method of preparing dense ceramic product[P].US:5188780,1991. |
| [5] | 陈大明;李斌太;杜林虎 等.一种制备陶瓷薄片的方法及专用模具[P].CN:01104148,1996. |
| [6] | 刘康时.陶瓷工艺学原理[M].广州:华南理工大学出版社,1990:119-120. |
| [7] | 沈继耀;胡宗民;谈家琪.电子陶瓷[M].北京:国防工业出版社,1979:130-131. |
| [8] | J CESARANO Ш;I A AKSAY .Processing of highly concentrated aqueous α-Al2O3 suspension with poly(Methacry acid) polyelectrolyte[J].Journal of the American Ceramic Society,1990,71(04):250-255. |
| [9] | 徐荣久 .电子陶瓷基片的新型制备技术[D].北京:北京航空材料研究院,1999. |
| [10] | 徐荣久;陈大明;周洋.球磨工艺对Al2O3陶瓷及瓷体性能的影响[A].杭州:科技导报社,2000:83-85. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%