研究了Al2O3/3wt%TiO2爆炸喷涂层的微观结构特征和纳米压痕力学特性.涂层的纳米压痕力学性能具有明显的各向异性行为和离散性.涂层表面比断面具有更为优良的抵抗外加负载和卸载后良好的弹性恢复的能力.表面和断面平均硬度分别为10.3GPa和2.9GPa,而表面和断面平均弹性模量分别为170.7GPa和234.5GPa.涂层各向异性的力学性能是由于爆炸喷涂的投影本质导致涂层断面的片层结构和平行于基体界面的裂纹形成.涂层断面比表面存在着尺度分布较宽的孔洞、裂纹等缺陷.
参考文献
| [1] | SOYKAN S;USTEL F;CELIK E et al.Investigation of friction and wear behaviours of plasma sprayed ceramic coating[J].Journal of Turkish Eng and Environ Sciences,1997,21:417-423. |
| [2] | You Wang;Stephen Jiang;Meidong Wang;Shihe Wang;T. Danny Xiao;Peter R. Strutt .Abrasive wear characteristics of plasma sprayed nanostructured alumina/titania coatings[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2000(2):176-185. |
| [3] | CALLUS P J;BERNDT C C .Relationships between mode II fracture toughness and microstructure of Thermal spray coatings[J].Surface and Coatings Technology,1999,111:114-128. |
| [4] | Kim JH.;Kim MC.;Park CG. .Evaluation of functionally graded thermal barrier coatings fabricated by detonation gun spray technique[J].Surface & Coatings Technology,2003(2/3):275-280. |
| [5] | AHMED R;HADFIELD M .Rolling contact fatigue performance of detonation gun coated elements[J].Tribology International,1997,30:129-137. |
| [6] | LI C J;OHMORI A .The lamellar structure of a detonation gun sprayed Al2O3 coating[J].Surface and Coatings Technology,1996,82:254-258. |
| [7] | TYURIN YU N;POGREBNJAK A D .Advanced in the development of detonation technologies and equipment for coating deposition[J].Surface and Coatings Technology,1999,111:269-275. |
| [8] | Kim JH.;Kim MC.;Park CG. .Evaluation of functionally graded thermal barrier coatings fabricated by detonation gun spray technique[J].Surface & Coatings Technology,2003(2/3):275-280. |
| [9] | KADYROV E;KADYROV V.Advanced gas detonation coating process DEMETON[A].Kobe, Japan:Japan High Temperature Society,1995:417-424. |
| [10] | 王俊,张立,李克,孙宝德,周尧和.爆炸喷涂Cr3C2-NiCr涂层及其在连铸辊上的应用[J].上海交通大学学报,2000(08):1018-1021. |
| [11] | SARAVANAN P;SELVARAJAN V;JOSHI S V et al.Experimental design and performance analysis of alumina coatings deposited by a detonation spray process[J].Journal of Physics D:Applied Physics,2000,123:44-54. |
| [12] | Gledhill HC;Turner IG;Doyle C .Direct morphological comparison of vacuum plasma sprayed and detonation gun sprayed hydroxyapatite coatings for orthopaedic applications.[J].Biomaterials,1999(4):315-322. |
| [13] | MURAKAMI Y;TANAKA K;ITOKAZU M et al.Elastic analysis of triangular pyramidal indentation by the finite-element method and ist application to nanoindentation measurement of glasses[J].Philosophical Magazine A:Physics of Condensed Matter:Structure,Defects and Mechanical Properties,1994,69:1131. |
| [14] | OLIVER W C;PHARR G M .An Improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments[J].Journal of Materials Research,1992,7:1564-1582. |
| [15] | Jeremy Thurn;Robert F. Cook .Simplified area function for sharp indenter tips in depth-sensing indentation[J].Journal of Materials Research,2002(5):1143-1146. |
| [16] | Woirgard J.;Riviere JP.;Dargenton JC.;Cabioc'h T. .Nanoindentation characterization of SiC coatings prepared by dynamic ion mixing[J].Surface & Coatings Technology,1998(1/3):128-131. |
| [17] | XU Zhi-hui;DAVID ROWCLIFFE .Nanoindentation on diamond-like carbon and alumina coatings[J].Surface and Coatings Technology,2002,161:44-51. |
| [18] | Standard Test Method for Microhardness of Materials[R].ASTM E384-89,1984. |
| [19] | MOODY N R;STROJNY A;MEDLIN D L et al.Substrate composition effects on the interfacial fracture of tantalum nitride films[J].Journal of Materials Research,1999,14:2306-2313. |
| [20] | KERNEN J;STENBERG T;MNTYL T et al.Microstructural characterization of detonation gun sprayed boride-based cermet coatings[J].Surface and Coatings Technology,1960,82:29-37. |
| [21] | M. Roy;C.V.S. Rao .Abrasive wear behaviour of detonation sprayed WC-Co coatings on mild steel[J].Surface Engineering,1999(2):129-136. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%