通过对两种成分单晶镍基合金进行蠕变曲线测定,长期时效处理及组织形貌观察,研究了元素W含量对单晶合金组织与性能的影响.结果表明:在Ni-A1-Cr-Ta-Co-x%W-5.5%Mo系单晶合金中,4wt%W合金在982℃,200MPa条件下,具有较长的蠕变寿命,随W含量增加到6wt%,合金的蠕变寿命明显降低.高W合金在有/无应力时效期间,析出针状μ相,使合金基体出现难溶元素的贫化区,是导致合金蠕变寿命降低的主要原因.其中μ相在(001)晶面沿<110>方向呈相互平行、或垂直的针状形貌析出,沿{111}晶面呈片状方式生长,且与γ′相相邻.
参考文献
| [1] | MACKAY R A;NATHAL MV;PEARSON D D .Influence of molybdenum on the creep properties of nickle-base superalloy single crystals[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1990,21:381-388. |
| [2] | J.D.Nystrom .Discontinuous Cellular Precipitation in a High-Refractory Nickel-Base Superalloy[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1997(12):2443-2452. |
| [3] | YU X H;YRO Y YAMABE-MITARAL;HARADA H.Design of quaternary Ir-Nb-Ni-Al refractory superalloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2000(31):173-178. |
| [4] | TIAN S G;XU Y B;HU Z O et al.Feature and effect factors of creep of single crystal nickel;-base superalloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2001,32:2947-2457. |
| [5] | NATHAL M V;EBERT L J .Influence of cobalt,tungsten on the elevated temperature mechanical properties of single crystal nickel base superalloys[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1985,16:1863-1870. |
| [6] | 郑运荣 .铸造镍基高温合金中的初生m相[J].金属学报,1999,35(12):1242-1245. |
| [7] | ZHAO K;MA Y H;LOU L H et al.Phase in a nickel base directionally solidified alloy[J].Materials Transactions,2005,46(01):54-58. |
| [8] | Simonetti M.;Caron P. .Role and behaviour of mu phase during deformation of a nickel-based single crystal superalloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):1-12. |
| [9] | ZHU J;YE H Q .On the microstructure and its diffraction anomaly of the μ phase in superalloys[J].Scripta Metallurgica et Materialia,1990,24:1861-1866. |
| [10] | 黄乾尧;李汉康.高温合金[M].北京:冶金工业出版社:80-82. |
| [11] | DAROLIA R;LAHRMAN D F;FIELD R D.Formation of topologically closed packed phases in nickel base single crystal superalloys[A].New York:TMS,1988:255-264. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%