研究马来酸酐接枝乙烯-辛烯共聚物弹性体(POE-g-MAH)和热塑性树脂(PC)协同增韧聚对苯二甲酸丁二酯的脆韧转变,借助扫描电镜(SEM)观察分析增韧体系的相形态和断口形貌,并对增韧机理进行探讨.结果表明,添加PC后,共混体系的脆韧转变在较低POE-g-MAH含量下发生.当PBT与PC质量配比为50/50时,共混物在POE-g-MAH含量为10%时获得超高韧性,达到78kJ/m2,同时拉伸强度达到52.5MPa.SEM分析认为,PC含量较高时,呈现极不规则的近似条状或片状的分散相结构,以及柔性界面层的存在是共混体系在较低弹性体含量下出现脆韧转变而获得高强韧性的主要机制.
参考文献
| [1] | HOBBS S Y;DEKKERS M E J;WATKINS V H .Toughened blends of poly(butylene terephthalate) and BPA polycarbonate,Part 1:Morphology[J].Journal of Materials Science,1988,23:1219-1224. |
| [2] | DEKKERS M E J;HOBBS S Y;WATKINS V H .Toughened blends of poly(butylene terephthalate) and BPA polycarbonate,Part 2:Toughening mechanisms[J].Journal of Materials Science,1988,23:1225-1230. |
| [3] | Jingshen Wu;Baohua Guo;Chi-Ming Chan;Jianxiong Li;Hoi-Shuen Tang .Synergistic toughening effect of SBS and HDPE on the fracture of the PS/HDPE/SBS blends[J].Polymer: The International Journal for the Science and Technology of Polymers,2001(21):8857-8865. |
| [4] | 周丽玲;吴其晔;杨文君.刚性有机粒子对聚氯乙烯/氯化聚乙烯共混体系形态和增韧机理的研究[J].高分子学报,1996(01):87-90. |
| [5] | 闫瑞萍;梁善杰 .PP/EPDM/HDPE三元共混材料的微观形态结构及增韧机理分析[J].工程塑料应用,1994,22(03):31-34. |
| [6] | 魏刚,黄锐,宋波.马来酸酐接枝乙烯-辛烯共聚物对聚对苯二甲酸丁二醇酯的增韧作用[J].合成橡胶工业,2004(02):115-115. |
| [7] | 罗毅;肖勤莎 .PBT工程塑料及其发展趋势[J].中国塑料,1998,12(01):9-14. |
| [8] | AROSTEGUI A;GAZTELUMENDI M;NAZABAL J .Toughened poly(butylenes terephthalate) by blending with a metallocenic poly(ethylene-octene) copolymer[J].Polymer,2001,42:9565-9574. |
| [9] | MARTIN P;DEVAUX J;LEGRAS R et al.Competitive reactions during compatibilization of blending of poly(butylenes terephthalate) with epoxide-containing rubber[J].Polymer,2001,42:2463-2478. |
| [10] | 董丽杰,张会轩,杨海东,熊传溪.EPM-g-GMA接枝率的测定及其增韧PBT的力学性能和形态结构研究[J].高分子学报,2003(02):167-170. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%