对平均粒度为60μm的Fe-Ni-Cu-C合金粗粉进行了注射成形.采用正交试验法,以生坯三点抗弯强度和生坯密度作为依据,研究了注射参数对生坯质量的影响,得到了理想的脱脂和烧结工艺.结果表明:在1225℃,H2和N2比为1∶3时得到的烧结件具有最好的力学性能,其抗拉强度为360MPa,屈服强度为171MPa,硬度为54HRB.
参考文献
[1] | GERMAN R M;HENS K F .Key issues in powder injection molding[J].Ceramic Bulletin,1991,70(08):1294-1302. |
[2] | GERMAN R M .Technological barriers and opportunities in powder injection molding[J].Powder Metallurgy International,1993,25(04):165-169. |
[3] | Kulkarni K.M.; .Future looking bright for PIM[J].Metal Powder Report,2000(10):40-42. |
[4] | CLIFFORD Ballard;MICHAEL Zedalis.Advances in powder injection molding[A].Atlanta:AN-TEC,1998:358-361. |
[5] | Paul A. Hauck .Powder injection molding: current and long term outlook[J].International Journal of Powder Metallurgy,2000(3):29-30. |
[6] | GERMAN R M .Scientific status of metal powder injection molding[J].International Journal of Powder Metallurgy,2000,36(03):31-36. |
[7] | 曲选辉,范景莲.纳米晶钨基重合金粉末的注射成型与固相烧浇[J].材料研究学报,2001(01):130-134. |
[8] | SUNG Hwan-Jin;HA Tae Kwon;AHN Sangho et al.Powder injection molding of a 17-PH stainless steel and the effect of sintering temperature on its microstructure and mechanical properties[J].Journal of Materials Processing Technology,2002,130-131:321-327. |
[9] | Zhu Baojun;Qu Xuanhui;Tao Ying .Powder injection molding of WC-8 percent Co tungsten cemented carbide[J].International Journal of Refractory Metals & Hard Materials,2002(5/6):389-394. |
[10] | Wenjea J. Tseng .Statistical analysis of process parameters influencing dimensional control in ceramic injection molding[J].Journal of Materials Processing Technology,1998(1/3):242-250. |
[11] | 乔斌;姬祖春;张永忠 .金属注射成形叶片式混炼机[J].辽宁工程技术大学学报(自然科学版),2006,25(zk):217-218. |
[12] | 乔斌,姬祖春,李映平,李化强,邹家生.金属注射成形新型混炼机的设计与制造[J].热加工工艺,2006(21):63-64. |
[13] | 李益民,黄伯云,张健,邱光汉,李松林.不同粉末对Fe-Ni合金注射成形工艺过程的影响[J].机械工程材料,2001(06):17-20. |
[14] | 李益民;曲选辉;邱光汉 等.注射成形Fe-Ni合金的机械性能和微观组织[J].中南大学学报(自然科学版),1997,28(03):250-253. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%