采用疲劳实验、SEM及TEM等分析测试手段,研究温度对2524-T4合金疲劳寿命及断裂机制的影响.实验结果表明,服役温度对合金疲劳寿命及断裂机制有显著的影响,温度升高导致合金在寿命106次条件下疲劳强度降低,100℃合金的疲劳强度较-55℃下降约30MPa.由于不同温度条件下疲劳过程中位错、二次相及晶界间相互作用机制的不同,-55℃条件下合金断裂表现出较强的晶体学裂纹特征,室温和高温条件下断口主要以穿晶断裂为主,同时伴随局部沿晶断裂特征.
参考文献
| [1] | C. P. Blankenship Jr;L. R. Kaisand .Elevated temperature fatigue crack propagation behavior of an Al-Li-Cu-Mg-Ag-Zr alloy[J].Scripta materialia,1996(9):1455-1460. |
| [2] | STRIVATSAN T S;SRIRAM S;DANILES C .Influence of temperature on cyclic stress response and fracture behavior of aluminum alloy 6061[J].Engineering Fracture Mechanics,1997,56(04):531-550. |
| [3] | C. GASQUERES;C. SARRAZIN-BAUDOUX;J. PETIT .Fatigue Crack Propagation in an Aluminium Alloy at 223 K[J].Scripta materialia,2005(12):1333-1337. |
| [4] | Majimel J;Casanove MJ;Molenat G .A 2xxx aluminum alloy crept at medium temperature: role of thermal activation on dislocation mechanisms[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):110-116. |
| [5] | STRIVATSAN T S;KOLAR D;MAGNUSEN P.The cyclic fatigue and final fracture behavior of aluminum alloy 2524[J].Materials & Design,2002(23):129-139. |
| [6] | William Cassada;John Liu;James Staley .ALUMINUM ALLOYS FOR AIRCRAFT STRUCTURES[J].Advanced Materials & Processes,2002(12):27-29. |
| [7] | Manabu Nakai;Takehiko Eto .New aspects of development of high strength aluminum alloys for aerospace applications[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(1/2):62-68. |
| [8] | JR STARKE E A;STALEYT J T .Application of modern aluminum alloys to aircraft[J].Progress in Aerospace Sciences,1996,32(2-3):131-172. |
| [9] | STRIVATSAN T S.An investigation of cyclic fatigue and fracture behavior of aluminum alloy 7055[J].Materials & Design,2002(23):141-151. |
| [10] | Ali Merati .A study of nucleation and fatigue behavior of an aerospace aluminum alloy 2024-T3[J].International Journal of Fatigue,2005(1):33-44. |
| [11] | GB 3075-1982.GB 3075-1982.金属轴向疲劳实验方法[S]. |
| [12] | HUNTER M S;FRICKE W G.Metallographic aspects of fatigue behavior of aluminium[J].Proceedings ASTM,1954(54):717-736. |
| [13] | EDWARDS P R;EARL M G.A comparative study of the fatigue performance of notched specimens of clad and unclad Aluminum alloy,with and without a pre-stress[A].Farnborough,1977:1361. |
| [14] | TRUCKNER W G;STALEY J T;BUCCI R J et al.Effect of microstructure on fatigue crack growth of high strength aluminum alloys[Technical Report AFML-TR-96169][R].USAF,1976. |
| [15] | 徐灏.疲劳强度[M].北京:高等教育出版社,1988 |
| [16] | 冯端.金属物理学Ⅲ:金属力学性质[M].北京:科学出版社,1999 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%