针对316L不锈钢进行大量单轴棘轮和蠕变试验研究,对材料在棘轮和蠕变作用下的塑性变形行为以及变形量进行比较和分析.分析发现,材料棘轮和蠕变变形行为之间存在一些相似规律,而且相同试验时间下蠕变变形高于棘轮变形.在持续应力作用下,材料的附加塑性变形与作用应力间体现出上凸的抛物线规律,附加塑性变形先随应力的增长而升高,达到峰值后又逐渐减小.最后,根据这种上凸的抛物线规律提出相应的本构描述方程.
参考文献
| [1] | CHABOCHE J L;NOUAILHAS D .Constitutive modeling of ratcheting effects-part Ⅰ:experimental facts and properties of the classical models[J].ASME Journal of Engineering Materials and Technology,1989,111:384-392. |
| [2] | OHNO N;WANG J -D .KINEMATIC Hardening rules with critical state of dynamic recovery,part Ⅰ:formulation and basic features for ratcheting behavior[J].Int Jof Plasticity,1993,9:375-390. |
| [3] | N. Ohno .Constitutive modeling of cyclic plasticity with emphasis on ratchetting[J].International Journal of Mechanical Sciences,1998(2/3):251-261. |
| [4] | 蔡力勋,牛清勇,刘宇杰.描述不锈钢材料单轴棘轮行为的一元参量体系[J].金属学报,2002(09):966-973. |
| [5] | 蔡力勋,牛清勇,刘宇杰,邱绍宇,李聪.应力循环下T225NG合金塑性累积行为研究[J].核动力工程,2004(04):352-356,365. |
| [6] | X.J. Yang;C.L. Chow;K.J. Lau .Time-dependent cyclic deformation and failure of 63Sn/37Pb solder alloy[J].International Journal of Fatigue,2003(6):533-546. |
| [7] | 康国政,孙亚芳,张娟,阚前华.SS304不锈钢在室温单轴循环加载下的时相关棘轮行为[J].金属学报,2005(03):277-281. |
| [8] | 阚前华,康国政,张娟,刘宇杰.SS304不锈钢高温非比例多轴加载下时相关循环变形行为的实验研究[J].金属学报,2005(09):963-968. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%