采用恒流微弧氧化法在碱性硅酸盐-磷酸盐体系电解液中对7A55铝合金进行了微弧氧化处理,研究了氧化时间对微弧氧化膜表面形貌、厚度和相组成的影响.研究结果表明,在恒定的电参数(电流密度为6A/dm2,占空比均为30%,频率为1000Hz)条件下,随着氧化时间的延长,阳极电压逐渐增大,氧化膜表面微孔孔径逐渐增大,微孔数量逐渐减少,膜层厚度随氧化时间近似呈线性增加;膜层主要由γ-Al2O3相组成.
参考文献
| [1] | Srivatsan TS.;Verraraghavan D.;Vasudevan VK.;Sriram S. .MICROSTRUCTURE, TENSILE DEFORMATION AND FRACTURE BEHAVIOUR OF ALUMINIUM ALLOY 7055[J].Journal of Materials Science,1997(11):2883-2894. |
| [2] | LUKASAK DA;HART RM .Aluminum alloy development efforts for compression dominated structure of aircraft[J].Light Metal Age,1991,49(9-10):11-15. |
| [3] | LIN J;KERSKER M M .Heat Treatment of Precipitation Hardening Alloys[P].United States Patent,5 108 520,1992-4-28. |
| [4] | R. Kaibyshev;T. Sakai;F. Musin .Superplastic behavior of a 7055 aluminum alloy[J].Scripta materialia,2001(12):1373-1380. |
| [5] | VOEVODIN A A;YEROKHIN A L;LYUBINOV V V.Characteration of wear rotective Al-Si-O coatings formed on Al based alloys by micro-arc discharge treatment[J].Surface and Coatings Technology,1996(86-87):516-621. |
| [6] | 薛文斌,邓志威,来永春,陈如意,张通和.有色金属表面微弧氧化技术评述[J].金属热处理,2000(01):1-3. |
| [7] | 姜兆华,辛世刚,王福平,吴晓宏,清水纪夫.铝合金在水玻璃-KOH-NaAlO2体系中的微等离子体氧化[J].中国有色金属学报,2000(04):519. |
| [8] | MCPHERSON R .The enthalpy of formation of aluminium titanate[J].Journal of Materials Science,1973,8:851-858. |
| [9] | Gnedenkov SV.;Zavidnaya AG.;Sinebrukhov SL.;Gordienko PS.;Iwatsubo S.;Matsui A.;Khrisanfova OA. .Composition and adhesion of protective coatings on aluminum[J].Surface & Coatings Technology,2001(1/3):146-151. |
| [10] | 吴振东,姜兆华,姚忠平,孙学通,张雪林.纯铝及其合金的微等离子体氧化成膜特征[J].中国有色金属学报,2005(06):946-951. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%