研究了快速凝固Mg-5Zn-1Y-0.6Zr合金在3.5%NaCl溶液中的腐蚀行为.利用金相显微镜、SEM观察了合金的微观组织和腐蚀形貌.结果表明,快速凝固使合金产生非晶相、晶粒细化及微观组织均匀,均对耐腐蚀性能提高起到作用.在室温下,腐蚀速率随时间先增大,随后逐渐减小.XRD分析表明腐蚀后的主要产物是Mg(OH)_2.通过极化曲线测试,表明合金耐蚀性能随冷却速率的提高而改善.
The effects of rapidly solidification on the microstructure and the corrosion behavior of Mg-5Zn-1Y-0.6Zr alloys in the 3.5% NaCl solution were investigated. The microstructure and the corrosion surface of the alloy were observed using OM and SEM. The results show that the amorphous phase occurred and alloy microstructures are refined and more uniformed by rapidly solidification,then the corrosion resistance of the alloy is improved. At room temperature, the corrosion rate increased firstly and then reduced with increase of time. The main corrosive product was mainly Mg(OH)_2 using XRD. Polarization curve test result shows the corrosion resistance is better as the cooling rate is higher.
参考文献
| [1] | 朱世杰,杨卿,白小波,王利国,关绍康.亚快速凝固Mg7Zn3Y（-Zr）合金的组织演化及凝固动力学[J].稀有金属材料与工程,2008(07):1157-1162. |
| [2] | D.K. Xu;W.N. Tang;L. Liu .Effect of Y concentration on the microstructure and mechanical properties of as-cast Mg-Zn-Y-Zr alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(1/2):129-134. |
| [3] | D.H. Bae;Y. Kim;I.J. Kim .Thermally stable quasicrystalline phase in a superplastic Mg-Zn-Y-Zr alloy[J].Materials Letters,2006(17/18):2190-2193. |
| [4] | Yingbo Zhang;Sirong Yu;Yulai Song .Microstructures and mechanical properties of quasicrystal reinforced Mg matrix composites[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2008(1/2):575-579. |
| [5] | D.H. Bae;M.H. Lee;K.T. Kim .Application of quasicrystalline particles as a strengthening phase in Mg-Zn-Y alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2002(1/2):445-450. |
| [6] | 黄晓梅,张春红,张密林.纯镁和镁锂合金在中性3.5%NaCl溶液中的腐蚀行为[J].航空材料学报,2008(03):71-76. |
| [7] | Michiaki Yamasaki;Naoyuki Hayashi;Shogo Izumi;Yoshihito Kawamura .Corrosion behavior of rapidly solidified Mg-Zn-rare earth element alloys in NaCl solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2007(1):255-262. |
| [8] | J. Cai;G.C. Ma;Z. Liu .Influence of rapid solidification on the microstructure of AZ91HP alloy[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2006(1/2):92-96. |
| [9] | 刘静远,张振忠,华旻,马立群,沈晓冬.快速凝固Mg-Zn-Y合金薄带的制备及凝固组织特征[J].铸造技术,2006(03):258-262. |
| [10] | 陈振华.镁合金[M].北京:化学工业出版社,2004 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%