采用透射电子显微镜、X射线衍射仪和纳米压痕仪对TC21钛合金表面喷丸强化层内的微观结构和纳米压痕力学性能进行了研究.结果表明,TC21钛合金表面经喷丸强化后,在表层形成一个弹塑性变形层.强化过程中由于密排六方晶体的基面、柱面和锥面滑移系的开动,造成位错密度升高,α相中位错形貌呈现网状;强化前纳米压痕硬度为3.2GPa,强化后为6.7GPa,提高1倍以上.在强化层内形成很高的宏观残余压应力,并且表现为由表面向里逐渐减少的梯度变化.强化层深度达到370μm.
参考文献
| [1] | 冯亮,曲恒磊,赵永庆,李辉,张颖楠,曾卫东.TC21合金的高温变形行为[J].航空材料学报,2004(04):11-13. |
| [2] | Fei, YH;Zhou, L;Qu, HL;Zhao, YQ;Huang, CZ .The phase and microstructure of TC21 alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):166-172. |
| [3] | 葛鹏,赵永庆,周廉.β钛合金的强化机理[J].材料导报,2005(12):52-55,63. |
| [4] | GAO Yu-kui;LI Xiang-bin;YANG Qing-xiang et al.Influence of surface integrity on fatigue strength of 40CrNi2Si2MoVA steel[J].Materials Letters,2006,61:466-469. |
| [5] | Y.-K. Gao;F. Lu;Y.-F. Yin .Effects of shot peening on fatigue properties of 0Cr13Ni8Mo2Al steel[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(3):372-374. |
| [6] | Wagner, L .Mechanical surface treatments on titanium, aluminum and magnesium alloys[J].Materials Science & Engineering. A, Structural Materials: Properties, Microstructure and Processing,1999(2):210-216. |
| [7] | 冯宝香,杨冠军,毛小南,于兰兰,吴小东.钛及钛合金喷丸强化研究进展[J].钛工业进展,2008(03):1-5. |
| [8] | 张建斌,马勤,周琦,王静宜.表面强化对工业纯钛显微组织的影响[J].中国有色金属学报,2001(06):1037-1040. |
| [9] | 高玉魁.喷丸对Ti-10V-2Fe-3Al钛合金拉-拉疲劳性能的影响[J].中国有色金属学报,2004(01):60-63. |
| [10] | 许顺生.金属X射线学[M].上海:上海科学技术出版社,1962 |
| [11] | 黄孝瑛.材料微观结构的电子显微学分析[M].北京:冶金工业出版社,2008 |
| [12] | 李超.金属学原理[M].哈尔滨:哈尔滨工业大学出版社,1989 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%