为了研究搅拌摩擦焊(FSW)对2195铝锂合金组织及性能的影响,对5mm薄板进行了不同工艺参数的搅拌摩擦焊接.显微组织分析及力学测试结果表明:合金经FSW后,接头组织由焊核区、热机影响区、热影响区三个明显不同的区域组成.当焊速不变,搅拌头转速ω在700～1300r/min之间变化时,接头抗拉强度随转速ω增大而降低;搅拌头转速不变,焊速υ在60～140mm·min-1之间变化时,接头抗拉强度随焊速υ增大而提高.当υ=140mm·min-1,ω=1000r/min时,焊接接头强度系数达到73%.焊后接头显微硬度发生了较大程度的软化.
参考文献
| [1] | Triolo A.;Lin JS.;Triolo R. .Early and late stages of demixing of a commercial Al-Li alloy[J].Journal of Materials Science,2002(6):1207-1213. |
| [2] | Zhen L.;Cui YX.;Shao WZ.;Yang DZ. .Deformation and fracture behavior of a RSP Al-Li alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):135-142. |
| [3] | GRININ V .Special features of welding thin sheet structures of 1420 alloy[J].WELDING PRODUCTION,1985,32(08):21-23. |
| [4] | M. N. James;D. G. Hattingh;G. R. Bradley .Weld tool travel speed effects on fatigue life of friction stir welds in 5083 aluminium[J].International Journal of Fatigue,2003(12):1389-1398. |
| [5] | BUSSU G;IRVING P E .The role of residual stress and heat affected zone properties on fatigue crack propagation in friction stir welded 2024-T351 aluminum joints[J].Internal journal of fatigue,2003,25(01):77-78. |
| [6] | 王希靖,李常锋,金玉花,张忠科.LY12搅拌摩擦焊焊缝成型及接头微观组织分析[J].热加工工艺,2006(23):24-27. |
| [7] | 王大勇,冯吉才,王攀峰.铝锂合金搅拌摩擦焊研究[J].材料科学与工程学报,2005(03):369-372. |
| [8] | 汪建华,姚舜,魏良武,戚新海.搅拌摩擦焊接的传热和力学计算模型[J].焊接学报,2000(04):61-64. |
| [9] | 王大勇,冯吉才,刘会杰.焊接速度对铝锂合金搅拌摩擦焊接头断裂特性的影响[J].焊接,2003(10):16-19. |
| [10] | 冯吉才,王大勇,王攀峰.锥形光头搅拌针搅拌摩擦焊接铝锂合金接头组织及力学性能[J].中国机械工程,2004(10):932-935. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%