采用显微硬度和力学性能测试及金相显微镜、扫描电镜、透射电镜、X射线衍射等分析手段,研究了Zn含量对Mg-10Gd-4.8Y-0.6Zr合金挤压以及时效处理后合金组织和力学性能的影响.结果表明,在Mg-10Gd-4.8Y-0.6Zr合金中添加Zn元素,有利于细化合金晶粒,提高挤压态的强度.未添加Zn的合金T5态晶粒尺寸约为25 μm,添加1％(质量分数,下同)Zn后,晶粒尺寸约为15μm,Zn含量为3％时,晶粒尺寸约为10μm.当Zn含量为1％时,合金挤压态和时效态的抗拉强度分别为337MPa,397MPa,屈服强度分别为128MPa,148MPa,伸长率分别为10.0％,5.0％,具有较好的综合性能.
参考文献
| [1] | MORDIKE B L;EBERT T .Magnesium properties-application-potential[J].Materials Science and Engineering,2001,302A(01):37-45. |
| [2] | 余琨,黎文献,王日初,马正青.变形镁合金的研究、开发及应用[J].中国有色金属学报,2003(02):277-288. |
| [3] | P. J. Apps;H. Karimzadeh;J. F. King;G. W. Lorimer .Phase compositions in magnesium-rare earth alloys containing yttrium, gadolinium or dysprosium[J].Scripta materialia,2003(5):475-481. |
| [4] | HE S M;ZENG X Q;PENG L M et al.Microstructure and strengthening mechanism of high strength Mg-10Gd2Y-0.5Zr alloy[J].Journal of Alloys and Compounds,2006,427(16):316-323. |
| [5] | YAO Su-juan;YI Dan-qing;YANG Sheng et al.Aging characteristics and high temperature tensile properties of Mg-Gd-Y-Zr alloys[J].Transactions of Nonferrous Metals Society of China,2007,42(07):418-422. |
| [6] | Mordike BL. .Creep-resistant magnesium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1-2 Special Issue SI):103-112. |
| [7] | S.M. He;X.Q. Zeng;L.M. Peng .Precipitation in a Mg-10Gd-3Y-0.4Zr (wt. percent) alloy during isothermal ageing at 250 deg C[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2006(1/2):309-313. |
| [8] | 肖阳,张新明,陈健美,蒋浩,邓桢桢.高强耐热Mg-9Gd-4Y-0.6Zr合金的性能[J].中南大学学报（自然科学版）,2006(05):850-855. |
| [9] | 陈振华.镁合金[M].北京:化学工业出版社,2004:30-31. |
| [10] | Z. Yang;J.P. Li;Y.C. Guo .Precipitation process and effect on mechanical properties of Mg-9Gd-3Y-0.6Zn-0.5Zr alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(0):274-280. |
| [11] | P.J. Apps;H. Karimzadeh;J.F. King .Precipitation reactions in Magnesium-rare earth alloys containing Yttrium, Gadolinium or Dysprosium[J].Scripta materialia,2003(8):1023-1028. |
| [12] | 张新明,陈健美,邓运来,肖阳,蒋浩,邓桢桢.Mg-Gd-Y-（Mn, Zr）合金的显微组织和力学性能[J].中国有色金属学报,2006(02):219-227. |
| [13] | Yan Gao;Qudong Wang;Jinhai Gu;Yang Zhao;Yan Tong .Behavior of Mg-15Gd-5Y-0.5Zr alloy during solution heat treatment from 500 to 540℃[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(1/2):117-123. |
| [14] | 刘林林,孙威,王飞,张泽.Mg-Gd-Y-Zn合金中长周期堆垛结构形成的原位准动态背散射电子显微研究[J].电子显微学报,2008(04):266-270. |
| [15] | Ke Liu .Effect of the long periodic stacking structure and W-phase on the microstructures and mechanical properties of the Mg-8Gd-xZn-0.4Zr alloys[J].Materials & design,2010(1):210-219. |
| [16] | XIAO Yang,ZHANG Xin-ming,CHEN Bu-xiang,DENG Zhen-zhen.Mechanical properties of Mg-9Gd-4Y-0.6Zr alloy[J].中国有色金属学会会刊（英文版）,2006(z3):1669-1672. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%