研究了四种不同二次时效热处理制度对β型阻燃钛合金Ti40力学性能的影响,并分析合金的微观组织.结果表明,延长550℃时效保温时间,合金塑性降低明显;时效温度从550℃提高到700℃,对塑性影响较大,特别是热暴露后的塑性降低较快;对相的分析表明其原因主要是时效时间的延长和温度的提高都会增加Ti5Si3相的析出与长大;但延长时效时间和提高时效温度可以有效提高材料的持久性能.
参考文献
| [1] | SEAGLE S R .The state of the USA titanium industry in 1995[J].Materials Science and Engineering,1996,A213:1-7. |
| [2] | BOYER R R .An overview on the use of titanium in the aerospace industry[J].Materials Science and Engineering,1996,A213:103-114. |
| [3] | LI Y G;BLENKINSOP P A;LORETTO M H et al.Structure and stability of precipitates in 500℃ exposed Ti-25V-15Cr-xAl alloys[J].Acta Materialia,1999,46(16):5777-5794. |
| [4] | LI Y G;LORETTO M H;RUGG D et al.Effect of heat treatment and exposure on microstructure and mechanical properties of Ti-25V-15Cr-2Al-0,2C alloy[J].Acta Materialia,2001,49:3011-3017. |
| [5] | 雷力明,黄旭,孙福生,曹春晓,D.Rugg,W.Voice.Ti-25V-15Cr-2Al-0.2C合金的组织、性能及其变形机制[J].中国有色金属学报,2003(04):939-943. |
| [6] | 雷力明,黄旭,孙福生,曹春晓,Rugg D,Voice W.热暴露对Ti-25V-15Cr-2Al-0.2C合金微观组织的影响[J].稀有金属,2003(01):207-209. |
| [7] | 黄旭,雷力明,王宝,赵红霞,曹春晓.Ti40合金热稳定性的研究[J].稀有金属,2004(01):44-46. |
| [8] | 雷力明,黄旭,孙福生,王宝,赵红霞,曹春晓.热处理对Ti-25V-15Cr-2Al-2Mo-0.2C合金组织稳定性的影响[J].稀有金属,2003(04):503-506. |
| [9] | 雷力明,黄旭,王宝,赵红霞.一种新型阻燃β钛合金的微观组织和力学性能研究[J].金属学报,2002(z1):138-141. |
| [10] | 赵永庆,曲恒磊,朱康英,吴欢,刘彩利,周廉.β型Ti40阻燃钛合金高温长期作用的第二相及其对性能的影响[J].稀有金属材料与工程,2002(02):84-88. |
| [11] | 辛社伟,赵永庆,曾卫东,吴欢.Ti40合金550 ℃热暴露组织和性能演化规律的分析与讨论[J].稀有金属材料与工程,2008(03):423-427. |
| [12] | ZHAO Y Q;ZHOU L .Mechanism of burn resistant of alloy Ti40[J].Journal of Materials Science and Technology,2001,17(06):677-678. |
| [13] | 雷力明 .低成本β稳定型阻燃钛合金的微观组织和力学性能研究[D].北京:北京航空材料研究院,2001. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%