利用Gleeble-3500型热模拟实验机,研究了TC4-DT损伤容限型钛合金在温度850℃ ～ 1000℃、应变速率0.01～ 10s-1、变形程度为40％ ～ 70％条件下的热变形行为,分析了该合金的流变应力行为及微观组织演变规律,并建立了本构关系模型.研究结果表明,TC4-DT合金在950℃以下的较低温度变形时应力软化现象非常明显,变形机制和热变形激活能不同于950℃以上的较高温度变形机制；在950℃以上高温度变形时,低应变速率(如(ε)=0.01s-1)促进了动态再结晶行为的发生,而在较高的应变速率(如(ε)=10s-1)时,一般只发生动态回复现象,动态再结晶行为受抑制.
参考文献
| [1] | C莱茵斯;M皮特尔斯.钛与钛合金[M].北京:化学工业出版社,2005:254-263. |
| [2] | 朱知寿;王庆如;郑永灵 .钛合金准β锻造工艺[P].中国专利号:ZL011312378,2004-7-28. |
| [3] | 李辉,曲恒磊,赵永庆,冯亮,曾卫东.片层厚度对损伤容限型TC21合金裂纹扩展速率的影响[J].材料工程,2006(04):21-23. |
| [4] | 李辉,赵永庆,曲恒磊,曾卫东.损伤容限型TC4-DT合金疲劳裂纹扩展行为研究[J].稀有金属材料与工程,2007(06):963-967. |
| [5] | 于兰兰,毛小南,李辉.温度对TC4-DT损伤容限型钛合金疲劳裂纹扩展行为的影响[J].稀有金属快报,2007(12):20-23. |
| [6] | 王新南,朱知寿,童路,周宇,周晓虎,俞汉清.锻造工艺对TC4-DT和TC21损伤容限型钛合金疲劳裂纹扩展速率的影响[J].稀有金属快报,2008(07):12-16. |
| [7] | B.X. Feng;X.N. Mao;G.J. Yang;L.L. Yu;X.D. Wu .Residual stress field and thermal relaxation behavior of shot-peened TC4-DTtitanium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009(1/2):105-108. |
| [8] | 吴超 .TA15钛合金β锻动态再结晶行为及其预测模型研究[D].南昌:南昌航空大学,2009. |
| [9] | Fei, YH;Zhou, L;Qu, HL;Zhao, YQ;Huang, CZ .The phase and microstructure of TC21 alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):166-172. |
| [10] | Zhao, Y.;Li, B.;Zhu, Z.;Nie, Z. .The high temperature deformation behavior and microstructure of TC21 titanium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(21/22):5360-5367. |
| [11] | Xiaoli Wang;Yongqing Zhao;Hongliang Hou;Yaoqi Wang .Effect of hydrogen content on superplastic forming/diffusion bonding of TC21 alloys[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2010(1):151-154. |
| [12] | 马少俊,吴学仁,刘建中,王利发.TC21钛合金的微观组织对力学性能的影响[J].航空材料学报,2006(05):22-25. |
| [13] | 刘杰;李落星;李光耀 等.AZ61镁合金高温变形应力修正及本构方程及建立[J].热加工工艺,2007,36(17):2-4. |
| [14] | SASTRYSM L;PAOPS;SANKARAN K K.High temperature deformation of Ti-6Al-4V[A].,1980:873-886. |
| [15] | Philippart I.;Rack HJ. .High temperature dynamic yielding in metastable Ti-6.8Mo-4.5Fe-1.5Al[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):196-200. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%