在着火热自燃理论基础上,通过分析钛颗粒表面氧化膜与基体之间的应力状态,结合实验事实,提出氧化膜最外层首先发生破裂但不形成贯穿裂纹的观点,基于该观点建立模型理论研究外层氧化膜的破裂行为对钛颗粒着火过程的影响,并对钛的着火过程进行物理模拟实验研究.结果表明:在673 ～1373K范围,当环境温度较低时,钛颗粒发生恒温氧化,氧化膜破裂导致氧化动力学曲线由抛物线向直线转化,当处于高温时,氧化膜的破裂使着火温度降低45K,不会对钛颗粒的着火过程产生强烈影响;当钛颗粒尺寸增大时,钛颗粒的着火温度未出现明显升高,与铝颗粒着火过程氧化膜的完全破裂机制不同;氧化膜内应力的变化使由外而内的裂纹扩展到一定程度后停止,即外层氧化膜不完全破裂,从而加速氧在内层氧化膜内扩散,增大了钛颗粒发生着火的敏感性;非等温氧化实验间接验证了外层氧化膜非贯穿破裂对钛着火过程影响的理论研究.
参考文献
| [1] | 黄旭,李臻熙,黄浩.高推重比航空发动机用新型高温钛合金研究进展[J].中国材料进展,2011(06):21-27. |
| [2] | BORISOVA Y A;SKLYAROV N M.Fireproof titanium alloys[J].Physical Metallurgy:New Alloyslished in Russia,1993(06):21-24. |
| [3] | ANDRZEJAK T A;SHAFIROVICH E;VARMA A .On the mechanisms of Ti particle reactions in O2 =N2 and O2 =Ar atmospheres[J].Propell Explos Pyrotech,2009,34:53-58. |
| [4] | GRACHUKHO V P;GUREVICH M A;SAVELEV M 1 .Ignition of isolated titanium particles in oxygen-containing media[J].Combustion Explosion and Shock Waves,1978,14(01):26-31. |
| [5] | Ervin Beloni;Edward L. Dreizin .IGNITION OF TITANIUM POWDER LAYERS BY ELECTROSTATIC DISCHARGE[J].Combustion science and technology,2011(7/9):823-845. |
| [6] | MERZHANOV A G .Thermal theory of metal particle ignition[J].AIAA Journal,1975,13(02):209-214. |
| [7] | KHAIKIN B I;BLOSHENKO V N;MERZHANOV A G .On the ignition of metal particles[J].Combustion Explosion and Shock Waves,1970,6(04):412-422. |
| [8] | KOVALEV V N;MELNIKOV V K .High-temperature oxidation and thermal ignition of titanium and zirconium plates[J].Combustion Explosion and Shock Waves,1978,14:279-285. |
| [9] | V. I. Bolobov .Mechanism of Self-Ignition of Titanium Alloys in Oxygen[J].Combustion, Explosion, and Shock Waves,2002(6):639-645. |
| [10] | V. I. Bolobov;N. A. Podlevskikh .Mechanism of Metal Ignition Due to Fracture[J].Combustion, Explosion, and Shock Waves,2007(4):405-413. |
| [11] | ROZENBAND V I;VAGANOVA N I .A Strength model of heterogeneous ignition of metal particles[J].Combustion and Flame,1992,88:113-118. |
| [12] | V. Rosenband .Thermo-mechanical aspects of the heterogeneous ignition of metals[J].Combustion and Flame,2004(3):366-375. |
| [13] | STRINGER J .The Oxidation of titanium in oxygen at high temperatures[J].Acta Metallurgica,1960,8(11):758-766. |
| [14] | Dimitris C. Lagoudas;Pavlin Entchev;Robertus Triharjanto .Modeling of oxidation and its effect on crack growth in titanium alloys[J].Computer Methods in Applied Mechanics and Engineering,2000(1/2):35-50. |
| [15] | KUBASCHEWSKI O;HOPKINS E B.Oxidation of metals and alloys[M].London:butterworth,1962 |
| [16] | KOFSTAD P;HAUFFE K;KJOLLESDAL H .Investigation on the oxidation mechanism of titanium[J].Acta Chemica Scandinavica,1958,12:239-266. |
| [17] | HANCOCK P;HURST R C .The mechanical properties and breakdown of surface oxide films at elevated temperatures[J].Advances in Corrosion Science and Technology,1974,4:1-84. |
| [18] | HSUEH C H;EVANS A G .Oxidation induced stresses and some effects on the behavior of oxide-films[J].Journal of Applied Physics,1983,54(11):6672-6686. |
| [19] | LUBLINER J.Plasticity Theory[M].New York:macmillan Publishing Company,1990 |
| [20] | STRAWBRIDGE A;EVANS H E .Mechanical failure of thin brittle coatings[J].Engineering Failure Analysis,1995,2(02):85-103. |
| [21] | HANCOCK P;NICHOLLS J R .Application of fracturemechanics to failure of surface oxide scales[J].Materials Science and Technology,1988,4(05):398-406. |
| [22] | JENKINS A E .A Further study of the oxidation of titanium and its alloys at high temperatures[J].Journal of the Institute of Metals,1955,84:1-9. |
| [23] | ROBERTSON J;MANNING M l .Limits to adherence of oxide scales[J].MaterSciTechn,1990,6:81-91. |
| [24] | VALENTIN N;MOISEYEV.Titanium Alloy:Russian Aircraft and Aerospace Applications[M].New York:crc Press,2006 |
| [25] | 莫畏.钛[M].北京:冶金工业出版社,2008 |
| [26] | Levitas VI;Asay BW;Son SF;Pantoya M .Mechanochemical mechanism for fast reaction of metastable intermolecular composites based on dispersion of liquid metal[J].Journal of Applied Physics,2007(8):83524-1-83524-20-0. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%