对热镀锌层上采用三价铬盐和三价铬盐加丙稀酸树脂两种钝化液钝化,探讨钝化液浓度、pH、钝化处理温度和时间对膜层耐腐蚀性能的影响.确定其钝化工艺,以取代六价铬盐钝化.试验结果表明,三价铬钝化液的最佳组分是将CrO3还原为三价铬,HNO3为氧化剂,硫酸和硼酸为添加剂.三价铬加丙烯酸树脂钝化液是以Cr2(SO4)3为主盐,次磷酸钠为络合剂,HNO3为氧化剂,硫酸和硼酸为添加剂,再加入与水的最佳体积比为1:3的丙烯酸树脂为最佳组成.采用三价铬盐或三价铬加丙稀酸树脂钝化均可推迟镀锌层出现白锈的时间,三价铬加丙烯酸树脂钝化液效果更好.
参考文献
| [1] | Nabil Zaki .TRIVALENT CHROME CONVERSION COATING FOR ZINC AND ZINC ALLOYS[J].Metal finishing,2002(1A):492-494,496-501-0. |
| [2] | Barnes C;Ward J J B;Sehmbhi T S .Non-chromate passivation treatment for zinc[J].Trans Imf,1982,60:45-48. |
| [3] | Klos Klaus P;Trebur .Process for chromating surface of zinc,cadmium and alloy there of[P].US 5368655,1994. |
| [4] | Paul C. Wynn;Craig V. Bishop .Replacing Hexavalent Chromium[J].Plating & Surface Finishing,2001(2):12-14. |
| [5] | 刘建军.三价铬钝化技术及其最新进展[J].电镀与环保,2002(06):22-23. |
| [6] | 吴以南.锌镀层的三价铬钝化[J].电镀与环保,2003(02):30-32. |
| [7] | Paramonov A;Filatova N G .Passivation of chrome-plated sheet iron in electrolytes based on chromium(Ⅲ) salt[J].Protection of Metal,2002,38(05):475-478. |
| [8] | 曾梁华.电镀与化学转化膜[M].北京:化学工业出版社,1994:3-18. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%