利用高压釜比较了P110、J55、1Cr3和0Cr13四种钢材在模拟油田产出水中抗CO2腐蚀的能力.发现随着实验时间的延长,前三种钢材的腐蚀速率逐渐下降,而0Cr13变化不大.它们的耐蚀性顺序为:0Cr13》1Cr3》J55》P110.利用SEM、XRD和能谱分析等方法解释了它们的腐蚀行为.
参考文献
| [1] | J K Heuer;J F Stubbins.An XPS Characterization of FeCO3 films from CO2 corrosion[J].Corrosion Science,1999(41):1231-1243. |
| [2] | 李静 .油管钢CO<,2>腐蚀行为与机理研究[D].北京科技大学,2001. |
| [3] | 赵国仙,严密林,路民旭,李平全.油田CO2腐蚀环境中的选材评价[J].腐蚀科学与防护技术,2000(04):240-242. |
| [4] | SY/T 5405-1996.SY/T 5405-1996.酸化用缓蚀剂性能试验方法及评价指标[S].,1996. |
| [5] | 张学元;邸超;雷良才.二氧化碳腐蚀与控制[M].北京:化学工业出版社,2000 |
| [6] | D A Lopez;T Perez;S N Simison .The influence of microstruture and chemical composition carbon and low alloy steels in CO2 corrosion.A state-of-the-art appraisal[J].Materials & Design,2003,24:561-575. |
| [7] | Lopez DA.;Schreiner WH.;de Sanchez SR.;Simison SN. .The influence of carbon steel microstructure on corrosion layers - An XPS and SEM characterization[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2003(1/4):69-85. |
| [8] | 陈长风,赵国仙,严密林,白真权,路民旭,杨延清.含Cr油套管钢CO2腐蚀产物膜特征[J].中国腐蚀与防护学报,2002(06):335-338. |
| [9] | 陈长风,路民旭,赵国仙,白真权,严密林,杨延清.含1%Cr的N80钢CO2腐蚀产物膜特征[J].中国腐蚀与防护学报,2003(06):330-334. |
| [10] | CO2腐蚀产物膜的微观形貌和结构特征[J].材料研究学报,2005(05):537-548. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%