本文简要阐述了影响烧结NdFeB系永磁材料矫顽力大小的因素以及其理想微结构,并着重介绍了添加元素和新工艺提高其矫顽力的方法.
参考文献
| [1] | 周寿增;董清飞.超强永磁体-稀土铁系永磁材料[M].北京:冶金工业出版社,1999 |
| [2] | 决定烧结NdFeB系永磁体矫顽力大小的因素[J].稀有金属快报,2002(08):1-2,28. |
| [3] | Fidler J;Schrefl T .Overview of Nd-Fe-F-B magnets and coereivity[J].Journal of Applied Physiology,1996(79):5029-5034. |
| [4] | 吴安国 .Nd-Fe-B烧结磁体的高性能化[J].磁性材料及器件,1998,29(04):12-18. |
| [5] | 张守民.NdFeB稀土永磁材料研究进展[J].稀土,2001(01):45-49. |
| [6] | Hanada Shigeki .Method for molding alloy powder for rare earth-iron-boron based permanent magnet[P].Japan Patent 4214803,1992. |
| [7] | Nishigori Thoshihisa .Manufacture of rare earth metal-iron based permanent magnet[P].Japan Patent:4191302,1992. |
| [8] | Ozaki Yukiko .Compacting assist agent of alloy powder for rare earth element series oermanent magnet[P].Japan Patent:4124202,1992. |
| [9] | Ge Xi-gan;Sun Chuan-qi .CHINA MAGNETS 98[R].thefifthreport,1998. |
| [10] | 梁树勇,李景宏,孙德成,陈风华.采用新工艺生产高性能烧结NdFeB永磁[J].磁性材料及器件,1999(02):29-33. |
| [11] | Bernardi J.;Sagawa M.;Hirose Y.;Fidler J. .Microstructural analysis of strip cast Nd-Fe-B alloys for high (BH)(max) magnets[J].Journal of Applied Physics,1998(11 Pt.2):6396-6398. |
| [12] | 韩劲;汪雨生 .烧结NdFeB铸造新工艺-薄片铸锭法[J].材料科学与工艺,1999,7:213-216. |
| [13] | 金瑞湘.高性能钕铁硼烧结磁体生产的一些新技术[J].金属功能材料,1999(05):197. |
| [14] | Takahashi M.;Taniguchi F.;Mikamoto T.;Uchida K. .High performance Nd-Fe-B sintered magnets made by the wet process[J].Journal of Applied Physics,1998(11 Pt.2):6402-6404. |
| [15] | H. Tokoro;K. Uchida .High energy product Nd-Fe-B sintered magnets produced by wet compacting process[J].IEEE Transactions on Magnetics,2001(4 Pt.1):2463-2466. |
| [16] | Akira Arai;Hiroshi Kato;Koji Akioka .Magnetic Properties of (Nd, Dy)-(Fe, Co)-B-Nb and Nd-(Fe, Co)-B Magnets Made by the Melt-Spinning Method With Grooved and Ceramic-Coated Roll[J].IEEE Transactions on Magnetics,2002(5):2964-2966. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%