以聚硅烷(PS)、聚氯乙烯(PVC)和钛酸四丁酯[Ti(OBu)4]合成含碳量不同的聚钛碳硅烷(PTC)先驱体，运用IR、GPC、VPO、TG等分析手段系统地研究了富碳PTC先驱体的合成及其组成结构，讨论了加入PVC含量不同对PTC合成及其结构、性能的影响。经熔融纺丝、不熔化处理、高温烧成制备出具有较好工艺性能和电阻率为100Ω*cm～103Ω*cm的富碳含钛碳化硅纤维(Si-Ti-C-O纤维)。
Polytitanocarbosilanes(PTC) with different C content are synthesized by polysilane(L.PS),polyvinyl chlo-ride(PVC) and Ti(OBu)4.The syntheses,composition and structme of the PTC with rich carbon are studied and the in-fluence of PVC content on the syntheses,composition,structure and properties of PIC is discussed by IR,GPC,VPO,TG.From these precursors,Si-Ti-C-O fibers with specific resistance of 1 Ω*cm ～ 103 Ω*cm are manufactured by melt spin-ning,curing in air and sintering at high temperature.
参考文献
| [1] | Yamamura T;Waku Y;Ishikawa T .[J].Journal of Materials Science,1988,23:2589-2594. |
| [2] | 王亦菲 .电阻率可调的Si-Ti-C-O纤维的制备及其结构、性能研究[D].国防科学技术大学,1998. |
| [3] | 王亦菲,冯春祥,宋永才.电阻率可调的含钛碳化硅纤维的制备与性能研究[J].宇航材料工艺,1999(01):28-31. |
| [4] | 王亦菲;冯春祥;宋永才 .电阻率可调的Si-Ti-C-O纤维的研制[J].高技术通讯,1999,9(05):45-49. |
| [5] | 王亦菲;冯春祥;宋永才;王应德 邹治春 .低电阻的si-Ti-C-O纤维性能研究[J].功能材料,1998,29:217-219. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%