在特定温度下,采用一定比例的氢氧化铝和磷酸合成出磷酸铝基体,对玻璃纤维或织物处理后,采用手糊工艺(固化温度低于220℃)制备了新型耐烧蚀复合材料--织物增强磷酸铝基复合材料.借助XRD和TG-DTA等测试技术,详细研究了材料的固化机理,发现材料可采用加热固化和常温固化.其热固化机理为:在加热时,酸式磷酸铝脱水形成聚合状的磷酸铝,然后转变为线型聚磷酸铝或环状偏磷酸铝;常温固化机理为:在常温下,酸式磷酸铝与活性适中的固化剂反应而获得强度.
参考文献
| [1] | 冯莉,段慎修,刘辉.磷酸盐耐热涂料的研制[J].涂料工业,2002(08):14-16. |
| [2] | 胡连成;黎义;于翘 .俄罗斯航天透波材料现状考察[J].宇航材料工艺,1994,24(01):50. |
| [3] | 张大海,黎义,高文,陈英,方超.高温天线罩材料研究进展[J].宇航材料工艺,2001(06):1-3. |
| [4] | Chase V A;Copeland R L .Development of a 1 200 °F radome[P].AD 429387 USA,1963. |
| [5] | Lyon J E;Fox T U;Lyons J W .An inhibited phosphoric acid for use in high-alumina refractories[J].Ceramic Bulletin,1966,45:661-665. |
| [6] | CASSIDY J E .Phosphate bonding then and now[J].Ceramic Bulletin,1977,56:640-643. |
| [7] | Mitsutomo Tsuhako;Tsuneo Matsuo.Formation of aluminium phosphates at low temperatures[M].Chemistry Letters,1978:777-780. |
| [8] | Morris J H;Perkins P G;Rose A E;Smith W E .Interaction between aluminium dihydrogen phosphate and quartz[J].Journal of Applied Chemistry and Biotechnology,1976,26:385-390. |
| [9] | 刘根荣 .Al2O3-P2O5-H2O和MgO-P2O5-H2O系统的相平衡及其在磷酸盐胶凝材料中的应用[J].硅酸盐学报,1980,8(01):38-53. |