采用融熔沉积快速成形法制备钛金属蜂窝结构材料,对粉浆制备、钛金属蜂窝结构蜡坯固化、脱蜡等工艺以及所制备的钛蜂窝体的压缩性能进行了研究.结果表明,采用融熔沉积快速成形可以制备钛金属蜂窝结构,工艺简单、尺寸可控,钛蜂窝结构的相对密度在9%～12.6%范围内,屈服强度和弹性模量的增加不大;相对密度超过12.6%后,屈服强度显著增加,但弹性模量增加的幅度不大.通过改变蜂窝体正六边形的边长或改变蜂窝体的壁厚均达到相同的相对密度条件下,蜂窝体的压缩强度差别不大,但对蜂窝体的弹性模量却有显著影响.
参考文献
| [1] | 陈勇军,左孝青,史庆南,宿罡,王茗.金属蜂窝的开发、发展及应用[J].材料导报,2003(12):32-35. |
| [2] | 曹斌升.航空发动机蜂窝结构的修理[J].焊接,1995(09):14-16. |
| [3] | Jongman Kim;Stephen R Swanson .Design of sandwich structures for concentrated loading[J].Computers & Structures,2001,52(3-4):365-373. |
| [4] | Gu S;Lu T J;Evans A G .On the design of two-dimensional cellular metals for combined heat dissipation and structural load capacity[J].Progress in Energy and Combustion Science,2004,30(06):545-672. |
| [5] | Lu T J .Heat transfer efficiency of metal honeycombs[J].International Journal of Heat and Mass Transfer,1998,42(11):2031-2040. |
| [6] | Haydn N. G. Wadley;Norman A. Fleck;Anthony G. Evans .Fabrication and structural performance of periodic cellular metal sandwich structures[J].Composites science and technology,2003(16):2331-2343. |
| [7] | 董希勤 .铝蜂窝结构件制造工艺与铝箔强度[J].宇航材料工艺,1994,24(04):30-33. |
| [8] | 陈衍祥;张海鸥;王桂兰.快速成形及其在快速制模中的应用[J].机电工程,1999(05):152-155. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%