为了提高C/E复合材料的导电性及耐空间环境的能力,应用电弧离子镀技术在C/E复合材料表面沉积了Al膜,研究了地面模拟原子氧环境对C/E复合材料表面镀Al前后的侵蚀、质损及Al膜的附着力、导电性的影响.通过XRD、SEM、FT-IR、万能拉伸测试仪、FZ-82 数字式四探针测试仪等测试分析样品.结果表明:电弧离子镀Al膜微米级以上颗粒较多,但分布均匀,膜层致密,附着力达2 N/mm2以上;原子氧对C/E复合材料侵蚀明显,镀铝后具有明显的防护作用;原子氧侵蚀后的Al膜电阻率有所上升,但还是有较好的导电性;辐照后的Al膜附着力比辐照前反而增加,其机理尚待进一步研究.
参考文献
| [1] | Trojaola M .[J].Sensors and Actuators A-physical,1993,37-38:233-238. |
| [2] | Burya A I;Cherkasova N G;Kazakov M E.[J].Fibre Composite Materials,2001(04):44-47. |
| [3] | Iskanderova Z;Kleiman J;Gudimenko Y et al.Nuclear Instruments and Methods in Phys[J].Research B,1997,127-128:702-709. |
| [4] | Haruvy Y .[J].European Space Agency Journal,1990,14(01):109-119. |
| [5] | Regnier N;Fontaine S .[J].Journal of Thermal Analysis and Calorimetry,2001,64:789-799. |
| [6] | Deev I S;Nikishin .[J].Composites Science and Technology,1997,57:1391-1401. |
| [7] | Babaevsky P G;Kozlov N A;Churilo I V et al.[J].Cosmic Research,2005,43(01):27-35. |
| [8] | 都亨;叶宗海.低轨道航天器空间环境手册[M].北京:国防工业出版社,1996 |
| [9] | Timothy K Minton;Jianming Zhang;Donna J Garton;James W Seale .Collision-assisted erosion of hydrocarbon polymers in atomic-oxygen environments[J].High performance polymers,2000(1):27-42. |
| [10] | Dobrovol′skayaI P;ChereiskiiZ Yu;Perepelkin K E et al.Fibre composite[J].Fibre Chemistry,2003,35(04):17-21. |
| [11] | 田民波;刘德令.薄膜科学与技术[M].北京:机械工业出版社,1991:174-178. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%